DuraForm® FR1200
- Chemical Family
- Polyamides
Properties
- Physical Form
- Powder
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Other Consumer Goods Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Other Automotive Applications
- Powertrain & UTH
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — 3D Printing Polymers
- Thermoplastic Powder
Other characteristics
- Brand
- DuraForm
- End Uses
Aerospace Applications, Aircraft Interiors, Automotive Applications, Automotive Exterior Parts, Automotive Interior Parts, Automotive Under The Hood, Computer Components, Consumer Applications
- Features
- Flame Retardant, Good Surface Finish
- Polymer Name
- Polyamide 12 (PA 12)
- Tensile Strength
- 41.0 - 41.0 MPa
- Processing Methods
- Selective Laser Sintering
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Flame Retardant
- Good Surface Finish
- Plastics and Elastomers End Uses
- Aerospace Applications
- Aircraft Interiors
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Automotive Under The Hood
- Computer Components
- Consumer Applications
- Plastics and Elastomers Processing Methods
- Selective Laser Sintering
Technical data
Table 1 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Sintered Part Density | 1.02 | g/cm3 | ASTM D792 |
| Water Absorption | 0.29 | — | ASTM D570 |
Table 2 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ultimate Tensile Strength | 41 | MPa | ASTM D638 |
| Hardness | 76 | Shore D | ASTM D2240 |
| Elongation at Break | 5.9 | % | ASTM D638 |
| Tensile Modulus | 2040 | MPa | ASTM D 638 |
| Ultimate Flexural Strength | 62 | MPa | ASTM D790 |
| Flexural Modulus | 1770 | MPa | ASTM D 790 |
| Notched Izod Impact Strength (23°C, 0.12) | 25 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C, 0.12) | 233 | J/m | ASTM D256 |
Table 3 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (0-145°C) | 140 | µm/m°C | ASTM E831 |
| Heat Deflection Temperature - HDT (0.45 MPa) | 180 | °C | ASTM D638 |
| Heat Deflection Temperature - HDT (1.82 MPa) | 94 | °C | ASTM D638 |
| Specific Heat Capacity (23°C) | 1.38 | J/g°C | ASTM E1269 |
| Specific Heat Capacity (50°C) | 1.68 | J/g°C | ASTM E1269 |
| Specific Heat Capacity (100°C) | 2.03 | J/g°C | ASTM E1269 |
| Specific Heat Capacity (150°C) | 2.51 | J/g°C | ASTM E1269 |
| Thermal Conductivity | 0.22 | W/(m K) | DIN 52616 |
Table 4 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dissipation Factor (1 kHz) | 0.038 | — | ASTM D150 |
| Surface Resistivity | 2.56E+13 | ohm/sq | ASTM D257 |
| Dielectric Constant (1 kHz) | 3 | — | ASTM D150 |
| Volume Resistivity | 597000000000000.0 | ohm-cm | ASTM D257 |
| Dielectric Strength | 22.6 | kV/mm | ASTM D149 |
Table 5 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (V2 at 5.0 mm) | Pass | — | UL 94V |
| Flammability (HB at 1.5 mm) | Pass | — | UL 94V |
| FAR 25.853 (a) and Appendix F Part I (b)(4) - 60 sec | 43 | mm | -- |
| FAR 25.853 (a) and Appendix F Part I (a)(1) - 12 sec | 2 | mm | -- |
| AITM 2.0006 Maximum Heat Release Rate (HRR) | 141.3 | kW/m2 | -- |
| AITM 2.0006 Total Heat Release (2min) | 105.2 | kW/m2 | -- |
| AITM 2.0007B Smoke Density Flaming Mode (12 sec) | Pass | — | -- |
| AITM 2.0007B Smoke Density Non Flaming Mode (3 sec) | Pass | — | -- |
| AITM 3.0005 Combustion Toxicity Flaming Mode | Pass | — | -- |
| AITM 3.0005 Combustion Toxicity Non Flaming Mode | Pass | — | -- |