DuraForm® ProX EX BLK
- Chemical Family
- Polyamides
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Other Consumer Goods Applications; Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Other Automotive Applications
- Powertrain & UTH
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- DuraForm
- Polymer Name
- Polyamide 11 (PA 11)
- Flexural Modulus
- 1360.0 - 1360.0 MPa
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Fatigue Resistant
- Impact Resistance
- Plastics and Elastomers End Uses
- Aerospace Applications
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Automotive Under The Hood
- Computer Components
- Consumer Applications
- Housings
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ultimate Tensile Strength | 43 | MPa | ASTM D638 |
| Hardness | 76 | Shore D | ASTM D2240 |
| Elongation at Break (5mm/min) | 60 | % | ASTM D638 |
| Elongation at Break (50mm/min) | 27 | % | ASTM D638 |
| Tensile Modulus | 1570 | MPa | ASTM D 638 |
| Ultimate Flexural Strength | 51 | MPa | ASTM D790 |
| Flexural Modulus | 1360 | Mpa | ASTM D790 |
| Notched Izod Impact Strength | 75 | J/m | ASTM D256 |
| Unotched Izod Impact Strength | 3336 | J/m | ASTM D256 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Sintered Part Density (23°C) | 1.02 | g/cm3 | ASTM D792 |
| Moisture Absorption (23°C) | 0.08 | % | ASTM D570 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (0-145°C) | 168 | µm/m°C | ASTM E831 |
| Heat Deflection Temperature - HDT (1.82 MPa) | 57 | °C | ASTM D648 |
| Heat Deflection Temperature - HDT (0.45 MPa) | 193 | °C | ASTM D648 |
| Specific Heat Capacity (23°C) | 1.77 | J/g°C | ASTM E1269 |
| Thermal Conductivity | 0.25 | W/m/K | — |
| Specific Heat Capacity | 1.77 | J/g°C | ASTM E1269 |
Table 4 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dissipation Factor (1 kHz) | 0.051 | — | ASTM D150 |
| Surface Resistivity | 2.53E+12 | ohm/sq | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.82 | — | ASTM D150 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Volume Resistivity | 1.09e+17 | ohm-cm | ASTM D257 |
Table 5 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Flammability | HB | UL 94 |