StructureWrap™ V2 200 Epoxy Resin
- Chemical Family
- Epoxy & Epoxy Derivatives
StructureWrap™ V2 200 Epoxy Resin is a two-component 100% solids, moisture-tolerant, highstrength, high modulus epoxy certified by ICC-ES as meeting building code requirements. It wasdeveloped specifically for use as the matrix resin in the StructureWrap™ V2 090 UC, V2 190UC, V2140 UG or the V2 280 UG systems.
Product families
Applications
- Structural Components
- Wall Panels
- Pavement Highways Roads & Bridges
Product Families
- Thermoset Resins
Other characteristics
- Brand
- StructureWrap
- End Uses
- Concrete Reinforcement, Structural Reinforcement
- Polymer Name
- Epoxy Resins & Compounds
- Markets
- Building & Construction
- Coverage
- As a sealer
- 100 ft²/gal
- As an impregnating resin
- 50-80 ft²/gal
- As a thickening tack coat
- 25 ft²/gal
- Coverage rates are based on a substrate with normal porosity
- First Aid
Eyes: Hold eyelids apart and flush thoroughly with water for 15 minutes. Skin: Remove contaminated clothing. Wash skin for 15 minutes with soap and water. Inhalation: Remove person to fresh air. Ingestion: Do not induce vomiting.
- PACKAGING
- 3 gallon kits
- 5 gallon kits
- 50 gallon drums
- Advantages
Long pot life and working time; Solvent free, VOC compliant; Moisture tolerant before, during and after cure; High strength, high modulus; Excellent adhesion to structural materials such as concrete, masonry, metal and wood; High temperature, abrasion and shock resistance; NSF/ANSI 61 approved for contact with potable water
- Shelf LIfe
- 1 year
- Limitations
Minimum substrate and ambient temperature 40°F (4°C) and rising; Do not thin with solvents; Material is a vapor barrier after cure; Concrete must be 28 days old
- Technology
- Composite Materials
- Labeling Claims
- Solvent-free
- VOC-free
- Composites End Use
- Concrete Reinforcement
- Structural Reinforcement
- Material Features
- Abrasion Resistant
- Excellent Elasticity
- Good Adhesion
- High Strength
- Shock Resistant
- Temperature Resistance
- Storage Condition
Store dry at 40°-90°F (4° -32°C)(Condition material to 65° -75°F (18° -24°C) before using)
- Composite Materials Functions
- Resins Binders & Matrix Materials
Technical data
Table 1 of 2
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (Min. 7 day cure at 73°F (23°C) and 50% R.H.) | 10,530 (72.6) | psi (MPa) | ASTM D-638 |
| Tensile Modulus (Min. 7 day cure at 73°F (23°C) and 50% R.H.) | 4.7 x 105 (3,240) | psi (MPa) | ASTM D-638 |
| Elongation at Break (Min. 7 day cure at 73°F (23°C) and 50% R.H.) | 2.25 | % | ASTM D-638 |
| Flexural Strength (Min. 7 day cure at 73°F (23°C) and 50% R.H.) | 18,000 (124) | psi (MPa) | ASTM D-638 |
| Flexural Modulus (Min. 7 day cure at 73°F (23°C) and 50% R.H.) | 4.6 x 105 (3,170) | psi (MPa) | ASTM D-638 |
Table 2 of 2
6 rows| Characteristic | Value | Unit |
|---|---|---|
| Mixing Ratio (by volumemix entire unit, do not batch) | 2:1 | — |
| Viscosity | 450 | cps |
| Pot Life (quart) | 4 | hours |
| Tack Free | 18 | hours |
| Glass Transition Temperature (after 72 hrs) | 150°F (65°C) | — |
| Service Temperature Range (-40° - 60°C) | -40°F - 140°F | — |