StructureWrap™ V2 190 UC
- Chemical Family
- Carbon Fiber
StructureWrap™ V2 190 UC is a proprietary high tensile strength, stitch bonded, unidirectional carbon fiber fabriccertified by ICC-ES as meeting building code requirements. The material is combined in the field utilizingStructureWrap™ V2 200 Epoxy to form a carbon fiber reinforced polymer (CFRP) laminate used to strengthenand/or upgrade structural elements.
Properties
- Physical Form
- Fabric
Product families
- Carbon Fiber
Other characteristics
- Brand
- StructureWrap
- Features
Acid Resistant, Acid resistance, Cost Effective, High Strength to Weight Ratio, High Tensile Strength, Light Weight, Lightweight
- Reinforcement Form
- Unidirectional Fabric
- Reinforcement Material
- Carbon Fibers
- Caution
StructureWrap V2 190 UC is non-reactive and non-toxic. However, caution must be used when handling since stray fibers and dust may be present on the surface. Gloves and the use of an appropriate properly fitted NIOSH approved respirator is recommended to prevent skin and lung irritation when handling, cutting and applying StructureWrap V2 190 UC.
- Markets
- Building & Construction
- Advantages
Certified by ICC-ES (ESR-3573); Meets ACI 440.2r-08 criteria; May be utilized to enhance shear, confinement or flexural strength; Can accommodate complex 3-D shapes; High strength to weight ratio; Light weight, adds negligible dead load to structure; Non-corrosive and non-magnetic; Acid and alkali resistant; Finished application does not change the esthetics of the structure
- Limitations
The installed system acts as a vapor barrier. Concrete should not be fully encapsulated in areas of freeze/thaw.
- Technology
- Composite Materials
- Labeling Claims
- Non-Corrosive
- Composites End Use
- Concrete Reinforcement
- Ducts
- Structural Reinforcement
- Material Features
- Acid Resistant
- Cost Effective
- High Strength to Weight Ratio
- High Tensile Strength
- Light Weight
- Composite Materials Functions
- Reinforcement
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Ultimate Tensile Strength Primary Fiber Direction (Ultimate Value, Design Value) | 1,414 (1,245) | Mpa |
| Tensile Modulus (Ultimate Value, Design Value) | 116,170 (116,170) | Mpa |
| Elongation at Break (Ultimate Value, Design Value) | 1.22 (1.07) | % (Mpa) |
| Flexural Strength (Ultimate Value, Design Value) | 814 (690) | Mpa |
| Compressive Strength (Ultimate Value, Design Value) | 499 (424) | Mpa |
Table 2 of 3
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Short Beam Shear (Ultimate Value, Design Value) | 45 (38) | Mpa |
| Glass Transition Temperature (Ultimate Value, Design Value) | 71.5 (71.5) | Mpa (°C) |
| Laminate Thickness (Ultimate Value, Design Value) | 0.850 (0.850) | Mpa (mm) |
Table 3 of 3
1 row| Characteristic | Value | Unit |
|---|---|---|
| Coefficient of Thermal Expansion (Ultimate Value, Design Value) | 50.07 (50.07) | Mpa (μm/m/°C) |