Original Material "S" ® plus+ GB
- Chemical Family
- PolyethylenesPolyolefins
Original Material "S" ® plus+ GB is used for applications that involve manufacturing and transportation at high pressure. The balance quantity of micro glass beads in Original Material "S" plus+® GB provide the combined benefits of extremely high molecular weight polyethylene and glass. The glass beads that protrude from the surface provide a rounded and hard sliding surface. A member of the S plus family Production based on PE-UHMW SG 1.1.
Product families
Applications
- Industrial — Other Industrial Applications
- Equipment & Parts
Product Families
- Polyolefins
Other characteristics
- Brand
- Original Material "S"
- Polymer Name
Ultra High Molecular Weight Polyethylene (UHMWPE)
- Fillers Included
- Glass Bead
- Markets
- Industrial
- Capability
Guides for PET bottle conveyors in the drinks industry In abrasive environments (for example, environments where lint is present).
- Technology
- Plastics
- Characteristics
High wear resistance; Extremely resistant to chemicals; Protects the sliding partner (unlike glass-fiber reinforced plastics); Very good resistance to chemicals; Approved for use in the food industry (EU and FDA)
- Material Features
- Chemical Resistant
- Certifications and Compliance
- EU Compliant
- FDA Compliant
- Plastics and Elastomers End Uses
- Pump Parts
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Average Coefficient of Friction against Steel⁶ (0.25 m/s, 0.25 N/mm²) | 0.2 | μ | — |
| Breaking Elongation | min. 250 | % | DIN EN ISO 5272 |
| Charpy Impact Strength (Two-sided Notch) | min. 100 | kJ/m² | DIN EN ISO 179 |
| Coefficient of Elasticity (Pulling Test) | min. 600 | MPa | DIN EN ISO 5272 |
| Hardness | 62 - 65 | Shore D | DIN EN ISO 868 |
| Indentation Hardness | min. 35 | MPa | DIN EN ISO 2039 |
| Sand-Slurry Test | 80 | % | DIN EN ISO 15527 |
| Yield Stress | approx. 20 | MPa | DIN EN ISO 5272 |
Table 2 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Code | PE - UHMW | — | ISO 10431 |
| Average Molecular Weight | 9 x 10⁶ | g/mol | — |
| Density | max. 0.94 | kg/dm³ | DIN EN ISO 11831 |
| Material Colour | Lime | — | — |
| Sheet Group | 1.1 | — | DIN EN ISO 15527 |
| Water Absorption (Saturation at 23°C) | max. 0.01 | % | — |
Table 3 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Burning behavior UL 94 (Sample thickness 3/6mm) | HB/HB | — | — |
| Heat Conductivity (23°C) | 0.4 | W/(K x m) | DIN 52612 |
| Linear Thermal Coefficient of Expansion α (Average Value between 23 and 60°C) | 17 x 10⁻⁵ | m/(K x m) | DIN EN ISO 113592 |
| Lower Service Temperature⁴ | -200 | °C | — |
| Melting Temperature | 130 - 135 | °C | DIN EN ISO 3146 |
| Upper Service Temperature Constant in Air (5000h) | 80 | °C | — |
| Upper Service Temperature Short-term (Air)² | 90 | °C | — |
Table 4 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Surface Resistance | min. 10¹² | Ω | IEC 60093 |
| Electric Strength | max. 45 | kV/mm | IEC 60243 |
| Specific Contact Resistance | min. 10⁻¹² | Ω x cm | IEC 60093 |