Addilene® J 430 N30
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
- Switches & Relays
- Terminal Blocks Plugs & Sockets
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Addilene
- Polymer Name
- Polypropylene Copolymer
- Fillers Included
- Mineral
- Note
The LOI measures are obtained through standard specimens of type I, with ignition of type A.. The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Plastics and Elastomers End Uses
- Electrical Components
- Electrical Housing
- Plugs
- Switches
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 6
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 20 | MPa | ISO 527 |
| Charpy Notched Impact Strength (at 23°C) | 10 | kJ/m2 | ISO 179-1/1eA |
| Hardness | 68 | Shore D | ASTM D 2240 |
| Hardness | 68 | Shore D | ISO 868 |
| Charpy Unnotched Impact Strength (at 23°C) | NB | kJ/m2 | ISO 179-1/1eU |
| Yield stress | 24 | MPa | ISO 527 |
| Strain at break | 15 | % | ISO 527 |
| Elongation at Break | min. 15 | % | ISO 527-2/1A |
| Flexural modulus, 23° | 2500 | MPa | ISO 178 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Izod Notched Impact Strength | 9 | kJ/m2 | ISO 180/1A |
| Charpy notched impact strength (+23°) | 10 | kJ/m2 | ISO 179/1eA |
Table 2 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (230°C/2.16 kg) | 13 | cm3/10 min | ISO 1133 |
| Density | 1140 | kg/m3 | ASTM D 792 |
Table 3 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (1.80 Mpa) | 62 | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Heat Deflection Temperature | 62 | °C | ISO 75-2/Af |
| Melting Point | 165/168 | °C | ISO 11357-3 |
| Vicat Softening Point | 152 | °C | ISO 306/A50 |
| Vicat softening temperature | 152 | °C | ISO 306 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| CTI | 600 | V | CEI 60112 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.14 | g/cm3 | ISO 1183-1 |
| MVI (at 230°C-2.16Kg) | 12 | cm3/10min | ISO 1133-1 |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Falling Ball Test | 125 | °C | CEI 60695-10-2 |
| Incandescent Glow Wire Flammability Test (2mm) | 750 | °C | CEI 60695-2-12 |