Addibio Renew® PMD 50659
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Biobased PP compound with visible natural fibers aspect. For SDS, please contact Addiplast Group using the 'Request Document' button.
Product families
Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Powertrain & UTH
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Addibio Renew
- Polymer Name
Polyolefin (unspecified), Polypropylene (unspecified); Polyolefin (unspecified); Polypropylene (unspecified)
- Fillers Included
- Natural Fiber
- Note
The LOI measures are obtained through standard specimens of type I, with ignition of type A.. The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Sustainable
- Material Features
- Good Aesthetics
- Light Weight
- Renewable Resource Content
- Certifications and Compliance
- California Proposition 65
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Automotive Instrument Panel
- Automotive Interior Parts
- Automotive Under The Hood
- Instrument Panel
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Notched Impact Strength (at -20°C) | 6 | kJ/m2 | ISO 179-1/1eA |
| Charpy Notched Impact Strength (at 23°C) | 15 | kJ/m2 | ISO 179-1/1eA |
| Charpy Unnotched Impact Strength (at -20°C) | 18 | kJ/m2 | ISO 179-1/1eU |
| Charpy Unnotched Impact Strength (at 23°C) | 25 | kJ/m2 | ISO 179-1/1eU |
| Elongation at Break | 7 | % | ISO 527-2/1A |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Izod Notched Impact Strength | 15 | kJ/m2 | ISO 180/1A |
| Shore D | 61 | — | ISO 868 |
| Stress at Break | 15 | MPa | ISO 527-2/1A |
| Stress at Yield Point | 20 | MPa | ISO 527-2/1A |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature | 75 | °C | ISO 75-2/Af |
| Melting Point | 165/168 | °C | ISO 11357-3 |
| Vicat Softening Point | 140 | °C | ISO 306/A50 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Post-Shrinkage | 0.71 - 1.44 | % | Méthode interne |
| Shrinkage | 0.69 - 1.43 | % | Méthode interne |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| CTI | min. 600 | V | CEI 60112 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1 | g/cm3 | ISO 1183-1 Méthode A |
| MVI (190°C-2.16kg) | 9 | cm3/10min | ISO 1133-1 |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Falling Ball Test | 110 | °C | CEI 60695-10-2 |