Additec® CJI 53081 NOIR 110 C
- Chemical Family
- Carbon FiberPolyolefinsPolypropylenes (PP)
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
Electrical & Electronics — Parts & Components
- Semiconductor Manufacturing
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Additec
- Polymer Name
- Polypropylene (unspecified)
- Fillers Included
- Carbon Fiber
- Note
The LOI measures are obtained through standard specimens of type I, with ignition of type A.. The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- ESD Protection
- High Modulus
- Low Density
- Semi Conductive
- Plastics and Elastomers End Uses
- Automotive Components
- Semiconductor Applications
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Notched Impact Strength (at 23°C) | 5 | kJ/m2 | ISO 179-1/1eA |
| Hardness | 72 | Shore D | ISO 868 |
| Charpy Unnotched Impact Strength (at 23°C) | 9 | kJ/m2 | ISO 179-1/1eU |
| Elongation at Break | 2 | % | ISO 527-2/1A |
| Flexural Modulus | 11500 | MPa | ISO 178 |
| Izod Notched Impact Strength | 5 | kJ/m2 | ISO 180/1A |
| Stress at Break | 51 | MPa | ISO 527-2/1A |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature | 135 | °C | ISO 75-2/Af |
| Melting Point | 165/168 | °C | ISO 11357-3 |
| Vicat Softening Point | 155 | °C | ISO 306/A50 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage | 0.13 | % | interne |
| Shrinkage | 0.79 | % | interne |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity | 10² - 10^4 | Ω-square | CEI 60093 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.04 | g/cm3 | ISO 1183-1 |
| MVI (at 230°C-2.16Kg) | 3 | cm3/10min | ISO 1133-1 |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Falling Ball Test | 135 | °C | CEI 60695-10-2 |