Addiflam® PMD 50445
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Flame retardant V2 homopolymer PP halogen free, UV stabilized. For SDS, please contact Addiplast Group using the 'Request Document' button.
Product families
Applications
Electrical & Electronics — Parts & Components
- Connectors
Electrical & Electronics — Wire & Cable
- Building Wires & Power Cables
- Other Wire & Cable Applications
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Addiflam
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Additives Included
- Flame Retardant
- Note
The LOI measures are obtained through standard specimens of type I, with ignition of type A.. The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.
- Markets
- Electrical & Electronics
- Flame Rating
- UL 94 V2
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Material Features
- Flame Retardant
- Non-Halogenated
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cables
- Electrical Connectors
- Wires
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Notched Impact Strength (at 23°C) | 3 | kJ/m2 | ISO 179-1/1eA |
| Hardness | 76 | Shore D | ISO 868 |
| Charpy Unnotched Impact Strength (at 23°C) | NB | kJ/m2 | ISO 179-1/1eU |
| Elongation at Break | min. 50 | % | ISO 527-2/1A |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Izod Notched Impact Strength | 3 | kJ/m2 | ISO 180/1A |
| Stress at Break | 20 | MPa | ISO 527-2/1A |
| Stress at Yield Point | 37 | MPa | ISO 527-2/1A |
Table 2 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature | 65 | °C | ISO 75-2/Af |
| Melting Point | 165/168 | °C | ISO 11357-3 |
| Vicat Softening Point | 155 | °C | ISO 306/A50 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| CTI | min. 600 | V | CEI 60112 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.9 | g/cm3 | ISO 1183-1 |
| MVI (at 230°C-2.16Kg) | 16 | cm3/10min | ISO 1133-1 |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Falling Ball Test | 138 | °C | CEI 60695-10-2 |
| Incandescent Glow Wire Flammability Test (2mm) | 960 | °C | CEI 60695-2-12 |
| Limit Oxygen Index | 26 | % | ISO 4589-2 |
| Vertical Burning (at 1.6mm) | V0 | — | Test 50W Ul94 |