Addilene® PMD 50384
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Product families
Applications
Applications
- Automotive & Transportation — Other Automotive & Transportation Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Addilene
- Polymer Name
- Polypropylene Copolymer
- Additives Included
- Impact Modifier
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Material Features
- Good Scratch Resistance
- Good Thermal Stability
- Heat Resistance
- Impact Modified
- Light Weight
- Low Emissions
- Low Odor
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Instrument Panel
- Automotive Interior Parts
- Consoles
- Door Panel
- Instrument Panel
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 17 | MPa | ISO 527 |
| Charpy Notched Impact Strength (at 23°C) | 18 | kJ/m2 | ISO 179-1/1eA |
| Strain at Break | min. 50 | % | ISO 527 |
| Hardness | 65 | Shore D | ISO 868 |
| Hardness | 65 | Shore D | ASTM D 2240 |
| Charpy Unnotched Impact Strength (at 23°C) | NB | kJ/m2 | ISO 179-1/1eU |
| Yield stress | 21 | MPa | ISO 527 |
| Elongation at Break | min. 50 | % | ISO 527-2/1A |
| Flexural modulus, 23° | 1050 | MPa | ISO 178 |
| Flexural Modulus | 1000 | MPa | ISO 178 |
| Izod Notched Impact Strength | NB | kJ/m2 | ISO 180/1A |
| Charpy impact strength (+23°) | N | kJ/m2 | ISO 179/1eU |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (230°C/2.16 kg) | 16 | cm3/10 min | ISO 1133 |
| Density | 900 | kg/m3 | ASTM D 792 |
Table 3 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (1.80 Mpa) | 52 | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Heat Deflection Temperature | 55 | °C | ISO 75-2/Af |
| Melting Point | 165/168 | °C | ISO 11357-3 |
| Vicat Softening Point | 140 | °C | ISO 306/A50 |
| Vicat softening temperature | 143 | °C | ISO 306 |
Table 4 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage | 1.6 | % | interne |
| Shrinkage | 1.7 | % | interne |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| CTI | min. 600 | V | CEI 60112 |
Table 6 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.9 | g/cm3 | ISO 1183-1 |
| MVI (at 230°C-2.16Kg) | 15 | cm3/10min | ISO 1133-1 |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Falling Ball Test | 120 | °C | CEI 60695-10-2 |