Addilene® H 220 M40
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Addilene
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Fillers Included
- Mineral
- Processing Methods
- Extrusion
- Note
The LOI measures are obtained through standard specimens of type I, with ignition of type A.. The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.
- Markets
- Consumer Goods
- Applications
Consumer Goods — Appliances & Electronics; Consumer Goods — Housewares; Consumer Goods — Other Consumer Goods Applications
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliance Components
- Appliances
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Notched Impact Strength (at 23°C) | 3.5 | kJ/m2 | ISO 179-1/1eA |
| Hardness | 76 | Shore D | ISO 868 |
| Charpy Unnotched Impact Strength (at 23°C) | 30 | kJ/m2 | ISO 179-1/1eU |
| Elongation at Break | 30 | % | ISO 527-2/1A |
| Flexural Modulus | 4000 | MPa | ISO 178 |
| Izod Notched Impact Strength | 3.5 | kJ/m2 | ISO 180/1A |
| Stress at Break | 27 | MPa | ISO 527-2/1A |
| Stress at Yield Point | 30 | MPa | ISO 527-2/1A |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature | 82 | °C | ISO 75-2/Af |
| Melting Point | 165/168 | °C | ISO 11357-3 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| CTI | min. 600 | V | CEI 60112 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.19 | g/cm3 | ISO 1183-1 |
| MVI (at 230°C-2.16Kg) | 3 | cm3/10min | ISO 1133-1 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Falling Ball Test | 142 | °C | CEI 60695-10-2 |
| Horizontal Burning (at 1mm) | HB | — | Test 50W Ul94 |