MAVEN MS 110
- Chemical Family
- Polyesters
Selenis Maven MS 110 is a copolyester with a slow crystallization rate and is suitable for the extrusion of heavy gage sheets, allowing for thicknesses up to 4mm, without crystallization occurring. Selenis Maven MS 110 is the most economic solution for flat sheets up to this thickness range, when good clarity, surface gloss, and neutral edge color are required.
Product families
- Thermoplastic Polyester Elastomers (TPE-E)
Other characteristics
- Brand
- MAVEN
- End Uses
Ceiling Panels, Decorative Displays, Displays, Door Panel, Instrument Panel, Wall Panels
- Polymer Name
- Copolyester Elastomer (COPE)
- Flexural Modulus
- 2214.0 - 2214.0 MPa
- Processing Methods
- Extrusion
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Paints & Coatings
- Features
Selenis Maven MS 110 is recommended when a combination of decorative capability, enhanced graphics, good impact strength at low temperatures and good chemical resistance to detergents and other household cleaning agents, are essential.. Selenis Maven MS 110 is easy to process on standard extrusion lines. Sheets made with Selenis Maven MS 110 may be personalized though different methods of decoration, due to its inherent surface tension. Selenis Maven MS 110 is BPA and styrene free and is fully recyclable code 1.
- Application
- Indoor and outdoor sign boards
- Panels for graphic arts
- Roofing
- Flat displays
- Technology
- Elastomers
- Labeling Claims
- Bisphenol A-free
- Recyclable
- Material Features
- Chemical Resistant
- Glossy Surface Aspects
- High Clarity
- Impact Resistance
- Recyclable
- Certifications and Compliance
- REACH (Europe)
- Plastics and Elastomers End Uses
- Ceiling Panels
- Decorative Displays
- Displays
- Door Panel
- Instrument Panel
- Wall Panels
- Safety Consideration
Read and follow all information presented in the Safety Data Sheet (SDS) for this product.
Technical data
Table 1 of 3
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Yield Stress (σy) | 59 | MPa | ISO 527 -1/- 2 |
| Elongation at Yield (ɛy) | 3.7 | % | ISO 527 -1/- 2 |
| Strength (σm) | 59 | MPa | ISO 527 -1/- 2 |
| Elongation at Strength (ɛm) | 3.7 | % | ISO 527 -1/- 2 |
| Nominal elongation at Break (ɛtb) | 353 | % | ISO 527 -1/- 2 |
| Flexural Modulus | 2214 | MPa | ISO 178 |
| Flexural Strength | 75 | MPa | ISO 178 |
| Notched 23ºC; 50% RH | 2.6 | kJ/m2 | ISO 180/A |
| Notched 0ºC; 50% RH | 2.6 | KJ/m2 | ISO 180/A |
| Notched -30ºC; 50% RH | 2.6 | KJ/m2 | ISO 180/A |
| Unnotched 23ºC; 50% RH | 122 | kJ/m2 | ISO 180/U |
| Unnotched 0ºC; 50% RH | 115 | KJ/m2 | ISO 180/U |
Table 2 of 3
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Intrinsic Viscosity | 0.84 - 0.88 | dl/g | ISO 1628-5 |
| Color b* | max. 0 | — | ASTM D6290 |
| Color L* | min. 85 | — | ASTM D6290 |
| Bulk Density | 0.84 | g/cm3 | — |
| Specific Density | min. 1.39 | g/cm3 | — |
| Water Absorption | max. 0.15 | % | ASTM D570 |
| Particle size | 270 - 370 | mg/20 chips | — |
| Pellet Shape | Cylindrical | — | — |
| Melting Point | 225 - 235 | °C | ASTM D3418 |
| Gloss (GU) | 155 | — | ASTM D2457/60º |
| Haze, 5 mm | max. 1.5 | % | ASTM D1003 |
| Acetaldehyde | max. 1 | ppm | ASTM F2013 |
Table 3 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature | 78 | ºC | ISO 306/A50 |
| Fire Behavior | DNI | — | ISO 3795 |