Staramide™ PF00AES
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 15000.0 - 15000.0 MPa
- Processing Methods
- Injection Molding
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Certifications and Compliance
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Stress at break | 210 | MPa | ISO 527 |
| Tensile Modulus | 16000 | MPa | ISO 527 |
| Strain at break | 2 | % | ISO 527 |
| Flexural modulus, 23° | 15000 | MPa | ISO 178 |
| Izod notched impact strength | 11 | kJ/m2 | ISO 180/1A |
| Izod impact strength, +23° | 55 | kJ/m2 | ISO 180/1U |
| Izod notched impact strength, +23° | 13 | kJ/m2 | ISO 180/1A |
| Rockwell Hardness | 114 | Scale L | ISO 2039-2 |
| Temperature | -40 | °C | — |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1580 | kg/m3 | ISO 1183 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 12 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 136 | E-6/K | ISO 11359-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 235 | °C | ISO 75-1/-2 |
| Thickness tested | 0.75 | mm | — |
| Vicat softening temperature | 240 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Table 4 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame rating | HB | UL 94 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 2.75 | % | Sim. to ISO 62 |
| Humidity absorption | 0.85 | % | Sim. to ISO 62 |