Staramide™ RF004XXC
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 6000.0 - 6000.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress at Yield (5 mm/min) | 120 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 2.2 | % | ISO 527-2/1A |
| Flexural Modulus | 6000 | MPa | ASTM D 790 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Izod Notched Impact Strength (80x10x4, 23°C) | 6 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 45 | kJ/m2 | ISO 180/1U |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar - Flow | 0.2 - 0.5 | % | E2P Method |
| Density | 1.28 | g/cm3 | ISO 1183/A |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT/Ae (1.8 MPa Edge 120x10x4 Sp=100mm) | 230 | °C | ISO 75/Ae |
Table 4 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | — |
| Mold Temperature | 60 - 90 | °C | -- |
| Drying Time | 4.0 - 6 | hrs | — |
| Front - Zone 3 Temperature | 270 - 290 | °C | — |
| Maximum Moisture Content | 0.2 | % | — |
| Melt Temperature | 270 - 290 | °C | — |
| Middle - Zone 2 Temperature | 270 - 280 | °C | — |
| Rear - Zone 1 Temperature | 260 - 280 | °C | — |