Staramide™ RFB33
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Bead, Glass Fiber
- Glass Bead
- Glass Fiber
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (1 mm/min) | 7000 | MPa | ISO 527 |
| Tensile Stress at Break (50 mm/min) | 128 | MPa | ISO 527 |
| Tensile Strain at Break (50 mm/min) | 2.6 | % | ISO 527-1,-2 |
| Flexural Modulus (2 mm/min) | 6000 | MPa | ISO 178 |
| Flexural Stress at Break (2 mm/min) | 185 | MPa | ISO 178 |
| Charpy V - Notch Edge (23°C, 80x10x4 Sp=62 mm) | 5.7 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | 46 | kJ/m2 | ISO 179/1eU |
| Izod Notched Impact Strength (80x10x4, 23°C) | 6 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 42 | kJ/m2 | ISO 180/1U |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage - Flow (4mm) | 0.2 - 0.4 | % | E2P Method |
| Density | 1.36 | g/cm3 | ISO 1183/A |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Point - DSC | 264 | °C | ISO 3146 |
| Heat Deflection Temperature - HDT (1.82 MPa, 3.2mm, Unannealed) | 230 | °C | ASTM D 648 |
Table 4 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Temperature | 70 - 90 | °C | -- |
| Drying Temperature | 70 - 80 | °C | — |
| Drying Time | 4.0 - 6 | hrs | — |
| Front - Zone 3 Temperature | 265 - 280 | °C | — |
| Maximum Moisture Content | 0.2 | % | — |
| Melt Temperature | 265 - 280 | °C | — |
| Middle - Zone 2 Temperature | 270 - 285 | °C | — |
| Rear - Zone 1 Temperature | 260 - 280 | °C | — |