Staramide™ RF004EU
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 6000.0 - 6000.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (1 mm/min) | 7000 | MPa | ISO 527 |
| Tensile Stress at Break | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain at Break | min. 3 | % | ISO 527 |
| Flexural Modulus | 6000 | MPa | ASTM D 790 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Charpy V - Notch Edge (23°C, 80x10x4 Sp=62 mm) | 7 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | 55 | kJ/m2 | ISO 179/1eU |
| Izod Notched Impact Strength (80x10x4, 23°C) | 8 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 48 | kJ/m2 | ISO 180/1U |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage - Flow (4mm) | 0.1 - 0.4 | % | E2P Method |
| Density | 1.28 | g/cm3 | ISO 1183/A |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT (1.82 MPa, 3.2mm, Unannealed) | 221 | °C | ASTM D 648 |
Table 4 of 4
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature | 75 - 85 | °C |
| Drying Time | 4.0 - 6 | hrs |
| Front - Zone 3 Temperature | 265 - 275 | °C |
| Maximum Moisture Content | 0.2 | % |
| Melt Temperature | 265 - 275 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 255 - 275 | °C |