Staramide™ RB006S

Name: Staramide™ RB006S
Brand: Staramide

Product families

Plastics — Engineering & Specialty Polymers

9 rows

Characteristic	Value	Unit	Method
Tensile Modulus (1 mm/min)	4500	MPa	ISO 527
Tensile Stress at Break (5 mm/min)	80	MPa	ISO 527-2/1A
Tensile Strain at Break (5 mm/min)	9	%	ISO 527
Flexural Modulus (2 mm/min)	4400	MPa	ISO 178
Flexural Stress at Break (2 mm/min)	130	MPa	ISO 178
Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm)	30	kJ/m2	ISO 179/1eU
Izod Notched Impact Strength (80x10x4, - 20°C)	3	kJ/m2	ISO 180/1A
Izod Notched Impact Strength (80x10x4, - 40°C)	2	kJ/m2	ISO 180/1A
Izod Notched Impact Strength (80x10x4, 23°C)	4	kJ/m2	ISO 180/1A

3 rows

Characteristic	Value	Unit	Method
Mold Shrinkage on Tensile Bar - Flow	1.1 - 1.5	%	E2P Method
Water Absorption (23°C/Sat)	5.5	%	ISO 62
Density	1.37	g/cm3	STANDARD ISO 1183

5 rows

Characteristic	Value	Unit	Method
HDT/Ae (1.8 MPa Edge 120x10x4 Sp=100mm)	100	°C	ISO 75/Ae
HDT/Be (0.45MPa Edge 120x10x4 Sp=100mm)	235	°C	ISO 75/Be
Coefficient of Thermal Expansion - Flow (23°C to 60°C)	4.0e-05	1/°C	ISO 11359-2
Coefficient of Thermal Expansion - Xflow (23°C to 60°C)	4.0e-05	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate A/50)	253	°C	ISO 306

1 row

Characteristic	Value	Unit	Method
Comparative Tracking Index - CTI	500	V	UL 746

2 rows

Characteristic	Value	Unit	Method
Oxygen Index - LOI	26	%	ISO 4589
Ul E2P Measurement, 94HB Flame Class Rating	1.6	mm	UL 94

8 rows