Starflam™ BFR552Y3
- Chemical Family
- Polyamides
Starflam BFR552Y3 is a Halogen and Red Phosphorous Free Flame Retardand, Glass Fiber Reinforced, Mineral Filled Polyamide 6 Injection Molding Resin
Properties
- Physical Form
- Pellets
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Starflam
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Flexural Modulus
- 5500.0 - 5500.0 MPa
- Additives Included
- Flame Retardant
- Processing Methods
- Extrusion, Injection Molding
- Flame Rating
- UL 94 V2
- Technology
- Plastics
- Labeling Claims
- Halogen-free
- Material Features
- Flame Retardant
- Low Odor
- Low Phosphorus Content
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Stress at break | 85 | MPa | ISO 527 |
| Tensile Modulus | 5800 | MPa | ASTM D 638 |
| Strain at break | 2.8 | % | ISO 527 |
| Flexural modulus, 23° | 5500 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 3 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 30 | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (-30°) | 2 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (-30°) | 25 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 4 | kJ/m2 | ISO 180/1A |
| Izod notched impact strength | 3 | kJ/m2 | ISO 180/1A |
| Temperature | -40 | °C | — |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1340 | kg/m3 | ASTM D 792 |
Table 3 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 45 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 70 | E-6/K | ISO 11359-1/-2 |
| Temperature of deflection under load (0.45 Mpa) | 210 | °C | ISO 75-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 180 | °C | ISO 75-1/-2 |
| Oxygen index | 24 | % | ISO 4589-1/-2 |
| Thickness tested | 0.75 | mm | — |
| Vicat softening temperature | 205 | °C | ISO 306 |
Table 4 of 5
1 row| Characteristic | Value | Method |
|---|---|---|
| Flame rating | V-2 | UL 94 |
Table 5 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Humidity absorption | 1.2 | % | Sim. to ISO 62 |