To catalogue
Staramide™ RB004
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Bead
- Flexural Modulus
- 3300.0 - 3300.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (1 mm/min) | 4300 | MPa | ISO 527 |
| Tensile Stress at Break | 65 | MPa | ISO 527-2 |
| Tensile Strain at Break | 5 | — | ISO 527-2 |
| Flexural Modulus | 3300 | MPa | ASTM D 790 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Charpy V - Notch Edge (23°C, 80x10x4 Sp=62 mm) | 4 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotch Edge (23°C, 80x10x4 Sp=62 mm) | 25 | kJ/m2 | ISO 179/1eU |
| Izod Notched Impact Strength (80x10x4, 23°C) | 4.5 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 25 | kJ/m2 | ISO 180/1U |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage - Flow (4mm) | 1.1 to 1.3 | % | E2P Method |
| Density | 1.29 | g/cm3 | ISO 1183 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT/Af (1.8 MPa Flatw 80x10x4 Sp=64mm) | 70 | °C | ISO 75/Af |
Table 4 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | — |
| Mold Temperature | 60 - 90 | °C | -- |
| Drying Time | 4.0 - 6 | hrs | — |
| Front - Zone 3 Temperature | 270 - 290 | °C | — |
| Maximum Moisture Content | 0.2 | % | — |
| Melt Temperature | 270 - 290 | °C | — |
| Middle - Zone 2 Temperature | 270 - 280 | °C | — |
| Rear - Zone 1 Temperature | 260 - 280 | °C | — |