To catalogue
Staramide™ RF00ASXS
- Chemical Family
- Polyamides
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Staramide
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (1 mm/min) | 15400 | N/mm2 | ISO 527-1 |
| Tensile Stress at Yield (5 mm/min) | 210 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 2.4 | % | ISO 527-2/1A |
| Flexural Modulus (2 mm/min) | 14100 | MPa | ISO 178 |
| Flexural Stress at Yield (2 mm/min) | 305 | MPa | ISO 178 |
| Izod Notched Impact Strength (80x10x4, 23°C) | 15 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (80x10x4, 23°C) | 80 | kJ/m2 | ISO 180/1U |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage - Flow (4mm) | 0.1 - 0.3 | % | E2P Method |
| Water Absorption (23°C/24 h) | 0.7 | % | ISO 62-1 |
| Density | 1.57 | g/cm3 | STANDARD ISO 1183 |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT/Af (1.8 MPa Flatw 80x10x4 Sp=64mm) | 246 | °C | ISO 75/Af |
| HDT/Bf (0.45 MPa Flatw 80x10x4 Sp=64mm) | 259 | °C | ISO 75/Bf |
| Coefficient of Thermal Expansion - Flow (23°C to 60°C) | 2.6e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion - Xflow (23°C to 60°C) | 8.4e-05 | 1/°C | ISO 11359-2 |
Table 4 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | — |
| Mold Temperature | 60 - 90 | °C | -- |
| Drying Time | 4.0 - 6 | hrs | — |
| Front - Zone 3 Temperature | 270 - 290 | °C | — |
| Maximum Moisture Content | 0.2 | % | — |
| Melt Temperature | 270 - 290 | °C | — |
| Middle - Zone 2 Temperature | 270 - 280 | °C | — |
| Rear - Zone 1 Temperature | 260 - 280 | °C | — |