BigRep PA6/66
- Chemical Family
- Polyamides
BigRep PA6/66 is a polyamide grade 3D printing filament combining excellent heat and chemical resistance, mechanical properties and printability.
Properties
- Physical Form
- Filament
Product families
Applications
Applications
- Industrial — Other Industrial Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
- Tooling & Moldmaking
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Automotive & Transportation — Transportation
- Aerospace & Aviation
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Polymer Name
- Polyamide 6/66 (PA 6/66)
- Flexural Modulus
- 1725.0 - 1725.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- Storage
Keep sealed in an air tight container, away from humidity.Store at around room temperature and protect from direct heat or sunlight. Material is sensitive to moisture and should be stored under dry conditions at all times
- Technology
- Plastics
- Material Features
- Chemical Resistant
- Durable
- Excellent Mechanical Strength
- Good Mechanical Properties
- Good Printability
- Heat Resistance
- HIGHLIGHTS
- Heat Resistance up to 180° C
- Chemical Resistance
- High Mechanical Strength
- Low-Weight Products
- Easily Machined
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Diameter | 2.85 | mm | — |
| Material | Polyamide 6/6.6 copolymer | — | — |
| Filament Net Weight | 3.0, 4.5, 8.0 | kg | — |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melting temperature | 190 | °C | DSC |
| Vicat Softening Temperature | 180 | °C | ISO 306 |
Table 2 of 3
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Young’s Modulus | 2325 | MPa | ISO 527 |
| Tensile Strength | 67 | MPa | ISO 527 |
| Elongation at break | 10 | % | ISO 527 |
| Bending Modulus | 1725 | MPa | ISO 178 |
| Bending Strenght | 98 | MPa | ISO 178 |
| Charpy Impact strength | 10 | kJ/m² | ISO 179 |
Table 3 of 3
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Nozzle temperature | 250 - 270 | °C |
| Heating bed temperature | 0 - 75 | °C |
| Environmental temperature | 40 - 60 | °C |
| Printing speed | min. 40 | mm/s |