Eurogrip STS
Eurogrip STS is a high friction ‘coat and scatter’ for used Ro-Ro ferry link spans and similar. It comprises a heavy duty polyurethane adhesive slurry with a surface scatter of high friction aggregate. This highly effective extra heavy duty surface is suitable for use by all types of vehicle and ‘tractor’. Suitable for use with 3-5 mm size high friction aggregate.
Product families
Applications
- Automotive OEM Coatings
Product Families
- Protective Coatings
Other characteristics
- Brand
- Eurogrip
- Features
Abrasion Resistant, Anti-Slip, High Friction, Long Shelf Life, Oil Resistant, Provides Solvent Resistance, Skid Resistant, Wear Resistant
- Product Type
- Coating
- Compatible Substrates & Surfaces
- Metal, Steel, Wood
- Markets
- Automotive & Transportation
- Benefits
Improved safety, better braking, better traction; Long service life compared with other similar systems; Minimal disruption to commercial operations - (rapid cure); Cold applied using mixer and squeegee; Low hazard materials; Reduced wear on vehicles; Resistant to oils and solvents; Combines high friction with waterproofing; Minimal maintenance; Suitable for a wide range of substrates (steel, bitumen, timber, etc); Low initial and whole life cost; Does not embrittle with age
- PACKAGING
Eurogrip STS is supplied in 25 kg units and in 3 components. Packaging is 3ltr pot (pack A), 10ltr pot (pack B) and 12kg bag (pack C). Aggregate is not included and must be purchased separately to the customers specific requirements for anti-skid performance, color and texture.
- Technology
- Ready-to-Use Products
- Packaging Type
- Bags
- Coverage and Cure
- Initial set @ 20°C -1 hour
- Open to traffic @ 20°C- 2½ hours
- Application Procedure
Strict compliance with the mixing and laying procedure is critical - mixing times must not be exceeded.Materials include Eurogrip STS which comes as 3 components. It is used in conjunction with the customer's chosen aggregate.; Pour the contents of Pack B into a suitable mixing vessel and mix using a drill and paddle until homogeneous. Whilst still mixing add the contents of Pack A and continue mixing for a further 20secs. Whilst still mixing slowly add the contents of Pack C and continue for 40 secs until a homogeneous mixture is achieved. Mix only one unit at a time. Pour the mixed material onto the surface and immediately spread using a serrated squeegee to the specified coverage (do not spread too thinly).; Broadcast the chosen aggregate onto the surface ensuring that there is no resin showing through. Remove any tape when resin starts to gel and excess aggregate when the surface becomes stable. This will vary with both product and ambient temperature.
Technical data
Table 1 of 1
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Adhesion to Steel (Pull-off Test at 5 days) | 5.0 | N/mm2 | BS 24624:1993 |
| Elongation at Break (After Curing for 14 days in Air) | min. 20 | % | BS 2782 Pt3 |
| Relative Density (20°C) | 1.6 | — | — |
| Tensile Strength (After Curing for 14 days in Air) | 12.0 | N/mm2 | BS 2782 Pt3 |