NGAC P907-01
- Chemical Family
- Epoxy & Epoxy Derivatives
NGAC P907-01 is a heat cured, low viscosity, rapid curing epoxy adhesive system designed specifically for use in the fiber optic industry.
Product families
Applications
Electrical & Electronics — Wire & Cable
- Optical Fiber & Telecom
Product Families
Ready-to-Use Products — Adhesives & Sealants
- Contact Adhesives
Other characteristics
- Brand
- NGAC
- Product Type
- Epoxy Adhesive
- Application Area
- Fiber Optic Cables
- Compatible Substrates & Surfaces
- Glass
- Markets
- Electrical & Electronics
- Storage
NGAC P907-01 packaged in XPAKs should be stored at 12 - 25°C, if crystallization of the resin occurs, place XPAK with pin in place in a 65°C oven for 15 minutes, allow to cool and proceed per normal procedures.
- PACKAGING
NGAC P907-01 packaged in PM&F syringes should be stored at -40°C.
- Advantages
NGAC P907-01 is a viscosity mixture that ensures exceptional wicking and wetting of the fibers, along with superior adhesion strength.
- Technology
- Ready-to-Use Products
- Cure Schedule
*For maximum physical properties a post-cure for 15 minutes at 120°C is recommended.
- Certifications
- GR-326 Certified
- Ready to Use Product Features
- Excellent Substrate Adhesion
- High Temperature Performance
- Low Viscosity
- Rapid Curing Speed
- Compatible Substrates and Surfaces
- Glass
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit |
|---|---|---|
| Specific Gravity | 1.2 | — |
| Viscosity | 250.0 | cps |
| Refractive Index | 1.56 | — |
| Spectral Transmittance (6000-9000 Å) | 93.0 | — |
| Water Absorption | 0.006 | % |
| Mix Ratio (Weight, R/H) | 100/10 | — |
| Hardness | min. 85 | Shore D |
| Operating Temperature | -60 to +175 | °C |
| Glass Transition (Tg, Ultimate) | 120.0 | °C |
| Volume Resistivity (23˚C) | > 1.5 x1010 | ohm-cm |
| Dielectric Strength | 400.0 | volts/mil |
| CTE (Alpha1, Below 120°C) | 5.88 x101 | ppm/°C |