SGF4950TT
- Chemical Family
- PolyethylenesPolyolefins
SGF4950TT is a copolymer high-density polyethylene specifically designed for the blow-molding segment. It does not contain optical brightener in its composition. This grade offers a well-balanced combination of impact and stiffness properties, along with high environmental stress cracking resistance and excellent processability. It has a minimum biobased carbon content of 96%, determined according to ASTM D6866.\nFor more information regarding REACH, please visit Braskem's REACH site
Product families
Applications
- Non-Food Consumer Packaging
Product Families
- Polyolefins
Other characteristics
- Brand
- I'm green bio-based
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 28.0 g/10 min
- Processing Methods
Blow Molding, Compression Molding, Extrusion Blow Molding (EBM)
- Note
Typical properties correspond to average values obtained in our laboratories. Test specimens prepared from compression molded sheet made according to ASTM D 4703. Thickness of test piece: a) 2 mm; b) 3 mm.
- Markets
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Low Carbon Footprint (PCF)
- Sustainable
- Sustainable Polyethylene
- Quality Standards
- In Preview
- Material Features
Good Environmental Stress Crack Resistance (ESCR); Good Impact Strength; Good Processability; Good Stiffness; Low Carbon Content
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- ENCS (Japan)
- IECSC (China)
- ISHL (Japan)
- KECI (Korea)
- NCI (Vietnam)
- NZIoC (New Zealand)
- Certifications and Compliance
- EC No.1907/2006
- Plastics and Elastomers End Uses
- Cosmetic Packaging
- Hygiene Packaging
- Tissue Packaging
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blow Molding
- Compression Molding
- Extrusion Blow Molding (EBM)
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 2.16kg) | 0.34 | g/10 min | ASTM D1238 |
| Density | 0.956 | g/cm³ | ASTM D792 |
Table 2 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 190°C, 21.6kg) | 28.0 | g/10 min | ASTM D 1238 |
| Tensile Strength (at Yield) ᵃ | 30.0 | MPa | ASTM D 638 |
| Tensile Strength (at Break) ᵃ | 30.0 | MPa | ASTM D 638 |
| Flexural Modulus (1% Secant) ᵇ | 1250.0 | MPa | ASTM D 790 |
| Tensile Impact Strength (at 23°C) | 110.0 | kJ/m² | ISO 8256 |
| Environmental Stress Cracking Resistance (Notch 0.3 mm, 50°C, 10% Igepal CO630) ᵃ | 30.0 | h/F50 | ASTM D 1693 |
| Deflection Temperature Under Load (at 0.455 MPa) ᵇ | 70.0 | °C | ASTM D 648 |
| Vicat Softening Temperature (at 10 N) ᵇ | 127.0 | °C | ASTM D 1525 |