Braskem America EB853
- Chemical Family
- PolyethylenesPolyolefins
Braskem EB853 low density polyethylene (LDPE) is produced under high pressure in a tubular reactor. Films obtained with this product show outstanding optical properties, good sealability, and low gel content.\nFor more information regarding REACH, please visit Braskem's REACH site
Properties
- Physical Form
- Pellets
Product families
Applications
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Polymer Name
- Low Density Polyethylene (LDPE)
- Melt Flow Index
- 2.7 g/10 min
- Processing Methods
- Cast Film Extrusion
- Note
Blown Film Properties (a) 40 µm thickness film in a 75mm screw diameter extruder with blow up ratio of 2.2:1. (MD: Machine Direction; TD: Transversal Directon)
- Markets
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Carbon Black-free
- Dye Free
- Pigment-free
- Material Features
- Good Optical Properties
- Good Sealant Properties
- Low Gel
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- EINECS (EU)
- ENCS (Japan)
- IECSC (China)
- ISHL (Japan)
- KECI (Korea)
- NZIoC (New Zealand)
- Certifications and Compliance
- ANVISA Resolution RDC No. 105/1999
- ANVISA Resolution RDC No. 326/2019
- ANVISA Resolution RDC No. 56/2012
- ANVISA Resolution RDC No. 91/2001
- Directive 1333/2008/EC
- EC No. 2023/2006
- EC No.1907/2006
- MERCOSUR GMC Resolution 39/19
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Cast Film Extrusion
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | D 792 |
| Melt Flow Rate (190°C/2.16 kg) | 2.7 | g/10 min | D 1238 |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dart Drop Impact Strength | 80 | g/F50 | D 1709 |
| Elmendorf Tear Strength (MD/TD) | 580/210 | gF | D 1922 |
| Elongation at Break (MD/TD) | 350/1050 | % | D 882 |
| Gloss - Angle 60º | 75 | % | D 2457 |
| Haze | 7 | % | D 1003 |
| Secant Modulus (1%) (MD/TD) | 145/150 | MPa | D 882 |
| Tensile Strength at Break (MD/TD) | 25/20 | MPa | D 882 |