Braskem America TI4005P2

Chemical Family: PolyolefinsPolypropylenes (PP)

Braskem TI4005P2 polypropylene impact copolymer (ICP) extra high Izod impact, very high flexural modulus, good low temperature drop impact, and is nucleated.\nAll Braskem America production facilities are certified to produce bio, bio-circular, and circular polypropylene under the ISCC PLUS certification via the mass balance approach.\nFor more information regarding REACH, please visit Braskem's REACH site

Properties

Physical Form: Pellets

Product families

Applications

Automotive & Transportation — Automotive

Other Automotive Applications

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Polymer Name: Polypropylene Impact Copolymer (ICP)
Melt Flow Index: 0.5 g/10 min
Additives Included: Nucleating Agent
Processing Methods: Compounding, Extrusion, Thermoforming
Markets: Automotive & Transportation
Technology: Plastics
Key Attributes: Exceptionally high Izod impact
Very high flexural modulus
Good low temperature drop impact
Nucleated
Labeling Claims: Bio-attributed
Bio-circular
Mass-balance
Sustainable
Material Features: Excellent Flexural Modulus
Extra High Izod impact
Low Temperature Impact Resistance
Certifications and Compliance: ISCC Plus
Plastics and Elastomers End Uses: Automotive Applications
Thermoforming Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Compounding
Extrusion
Thermoforming

Technical data

Table 1 of 2

6 rows

Characteristic	Value	Unit	Method
Elongation at Yield (2 in/min, 50 mm/min)	10.5	%	ASTM D-638
Flexural Modulus (0.05 in/min, 1.3 mm/min, 1% secant)	1,448	MPa	ASTM D-790A
Notched Izod Impact Strength (at 23°C)	No Break	—	ASTM D-256A
Rockwell Hardness	78	R	ASTM D-785
Tensile Strength at Yield (2 in/min, 50 mm/min)	29	MPa	ASTM D-638
Instrumented Impact Strength (at -29Â°C)	49	J	ASTM D-3763

Table 2 of 2

1 row

Characteristic	Value	Unit	Method
Nominal Melt Flow (230°C/2.16kg)	0.5	g/10 min	ASTM D-1238