Braskem America HDB6050
- Chemical Family
- PolyethylenesPolyolefins
Braskem HDB6050 is a high molecular weight copolymer grade developed for the production of medium large blow molded articles. It provides excellent processability, good rigidity, outsanding chemical resistance, high impact strength and high enviromental stress cracking resistance (ESCR).\nFor more information regarding REACH, please visit Braskem's REACH site
Product families
Applications
Printing & Packaging — Packaging
- Industrial & Transport Packaging
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Polymer Name
- Polyethylene Copolymer
- Melt Flow Index
- 5.0 g/10 min
- Processing Methods
- Blow Molding
- Markets
- Printing & Packaging
- Technology
- Plastics
- Material Features
Good Environmental Stress Crack Resistance (ESCR); Good Impact Strength; Good Processability; Good Rigidity
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blow Molding
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Charpy Impact Strength (Test Temperature at 23°C) | 25 | °C | ISO 179-1EA |
| Elasticity Modulus (Secant 1%) | 1125 | MPa | ASTM D-638 |
| Elongation at Break | 664 | % | ASTM D-638 |
| Environmental Stress Cracking Resistance (10% Igepal, Condition B) | 190 | h | ASTM D-1693 |
| Environmental Stress Cracking Resistance(100% Igepal, Condition B) | min. 1000 | h | ASTM D-1693 |
| Flexural Modulus (Secant 1%) | 1090 | MPa | ASTM D-790 |
| Izod Impact Strength (at 23°C) | 553 | J/m | ASTM D-256/A |
| NCLS | 260 | h | ASTM F2136 |
| Tensile Strength at Break | 40 | MPa | ASTM D-638 |
| Tensile Strength at Yield | 22 | MPa | ASTM D-638 |
Table 2 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 0.95 | g/cm³ | ASTM D-792 |
| Melt Flow Rate (190°C/21.6Kg) | 5 | g/10 min | ASTM D-1238 |