Polymer Resources Ltd. PRL TP-G30
- Chemical Family
- Polyesters
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Healthcare & Pharma — Medical
- Medical Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Features
- Good Dimensional Stability
- Good Stiffness
- High Heat Resistance
- Availability
- North America
- Technology
- Plastics
- Processing Method
- Injection Molding
- Quality Standards
- UL Yellow Card (E113219)
- Material Features
- Dimensional Stability
- Good Stiffness
- Heat Resistance
- UL Flame Rated
- Country Availability
- Canada
- Mexico
- USA
- Filler/Reinforcement
- Filler
- Glass Fiber
- Reinforcement
- 30% Filler by Weight
- Agency Ratings
- RoHS Compliant
- Certifications and Compliance
- RoHS Compliant
- Plastics and Elastomers End Uses
- Appliances
- Medical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.52 | — | ASTM D792 |
| Melt Mass Flow Rate (at 250°C, 2.16 kg) | 8.0 - 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage (at 0.125 in, Flow) | 6.0E-3 to 9.0E-3 | in/in | ASTM D955 |
| Specific Gravity | 1.52 | — | ASTM D792 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength (at Yield, 0.125 in) | 17000 | psi | ASTM D638 |
| Tensile Strength (at Break, 0.125 in) | 17000 | psi | ASTM D638 |
| Flexural Modulus (at 0.125 in) | 1100000 | psi | ASTM D790 |
| Flexural Strength (at Break, 0.125 in) | 28000 | psi | ASTM D790 |
Table 3 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) | 425 | °F | ASTM D648 |
| Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) | 395 | °F | ASTM D648 |
| Relative Thermal Index Electrical Property (at 0.06 in) | 167 | °F | UL 746 |
| Relative Thermal Index Electrical Property (at 0.12 in) | 167 | °F | UL 746 |
| Relative Thermal Index Impact Property (at 0.06 in) | 167 | °F | UL 746 |
| Relative Thermal Index Impact Property (at 0.12 in) | 167 | °F | UL 746 |
| Relative Thermal Index Strength Property (at 0.06 in) | 167 | °F | UL 746 |
| Relative Thermal Index Strength Property (at 0.12 in) | 167 | °F | UL 746 |
Table 4 of 7
5 rows| Characteristic | Value | Method |
|---|---|---|
| Comparative Tracking Index (at 0.0591 in) | PLC 1 | UL 746 |
| High Amp Arc Ignition (at 0.06 in) | PLC 2 | UL 746 |
| High Amp Arc Ignition (at 0.12 in) | PLC 2 | UL 746 |
| Hot Wire Ignition (at 0.06 in) | PLC 2 | UL 746 |
| Hot Wire Ignition (at 0.12 in) | PLC 1 | UL 746 |
Table 5 of 7
2 rows| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (at 0.06 in) | HB | UL 94 |
| Flame Rating (at 0.12 in) | HB | UL 94 |
Table 6 of 7
8 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature | 240 - 250 | °F |
| Drying Time | 3.0 - 4.0 | hr |
| Front Temperature | 480 - 510 | °F |
| Middle Temperature | 470 - 500 | °F |
| Mold Temperature | 150 - 190 | °F |
| Rear Temperature | 460 - 490 | °F |
| Maximum Drying Time | 8 | hr |
| Processing Temperature (Melt) | 450 - 500 | °F |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Impact Strength (at 73°F, 0.125 in, Notched Izod) | 1 | ft·lb/in | ASTM D256 |