Bio-Flex® S 5630
- Chemical Family
- PolyestersPolylactic Acid (PLA)
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Bio-Flex
- Polymer Name
- Copolyester Resin, Polylactic Acid (PLA)
- Copolyester Resin
- Polylactic Acid (PLA)
- Flexural Modulus
- 2400.0 - 2400.0 MPa
- Processing Methods
- Film Extrusion, Injection Molding, Thermoforming
- Color
- White
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Printing & Packaging
- Technology
- Plastics
- Quality Standards
- Other Quality Standards
- Material Features
- Low Odor
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers End Uses
- Cosmetic Packaging
- Machine/Mechanical Parts
- Thermoforming Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Film Extrusion
- Injection Molding
- Thermoforming
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 32 | MPa | ISO 527 |
| Stress at break | 29 | MPa | ISO 527 |
| Tensile Modulus | 2160 | MPa | ISO 527 |
| Strain at break | 9 | % | ISO 527 |
| Flexural modulus, 23° | 2400 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 3 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 51 | kJ/m2 | ISO 179/1eU |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (190°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 9 | cm3/10 min | ISO 1133 |
| Molding shrinkage - parallel | 0.5 | % | ISO 294-4, 2577 |
| Density | 1550 | kg/m3 | ASTM D 792 |
Table 3 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (0.45 Mpa) | 68 | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 150 | °C | ISO 11357-1/-3 |
| Vicat softening temperature | 105 | °C | ISO 306 |
Table 4 of 4
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Biobased content | 20 | % |
| Bulk density | 895 | kg/m3 |