Bio-Flex® F 1137
- Chemical Family
- PolyestersPolylactic Acid (PLA)
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- Bio-Flex
- Polymer Name
- Polylactic Acid (PLA)
- Flexural Modulus
- 305.0 - 305.0 MPa
- Processing Methods
- Film Extrusion
- Color
- White
- Technology
- Plastics
- Quality Standards
- Other Quality Standards
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- ISO 9001
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Film Extrusion
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 15.5 | MPa | ISO 527 |
| Strain at Break | min. 50 | % | ISO 527 |
| Stress at break | 13.8 | MPa | ISO 527 |
| Tensile Modulus | 310 | MPa | ISO 527 |
| Flexural modulus, 23° | 305 | MPa | ISO 178 |
| Charpy impact strength (+23°) | N | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | N | kJ/m2 | ISO 179/1eA |
Table 2 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (190°C/2.16 kg) | 3.25 | g/10 min | ISO 1133 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 2.5 | cm3/10 min | ISO 1133 |
| Density | 1470 | kg/m3 | ASTM D 792 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting temperature (10°C/min) | 155 | °C | ISO 11357-1/-3 |
Table 4 of 4
1 row| Characteristic | Value | Unit |
|---|---|---|
| Biobased content | 10 | % |