SuperSeal™ 2000
- Chemical Family
- Acrylics & Acrylates
SuperSeal™ 2000 is an acrylic-based, crystal-clear sealer. Formulated and recommended for application to a porous substrate for the primary purpose of preventing the penetration of water. It is a premium-quality, non-yellowing, UV resistant, super-tough acrylic film that is easy to clean and maintain. It is formulated and recommended for application to a porous substrate for the primary purpose of preventing the penetration of water.
Other characteristics
- Brand
- SuperSeal
- Features
Consistent High Quality, Excellent Transparency Properties, Glossy Surface Aspects, Good Non-Yellowing Properties, Good Toughness, Good UV Resistance. Non Yellowing, Crystal Clear Dries to a Gloss "Wet Look" Finish Interior/Exterior Use- Enhances Color.
- Product Type
- Sealer
- Application Method
- Roller, Spray
- Compatible Substrates & Surfaces
- Concrete
- Usage
SuperSeal™ 2000 can be used on interior or exterior masonry, and concrete-type surfaces. SuperSeal™ 2000 can be used as a base-coat for interior applications where a compatible, commercial floor waxes is planned as part of a maintenance program. Use on colored or uncolored, stamped or exposed aggregate concrete, porous brick, natural and manufactured stone, stucco, slate, unglazed tile and flagstone.
- Markets
- Building & Construction
- Storage
Store in a safe place. Keep containers tightly sealed. DO NOT allow product to freeze. Material that is froz CANNOT be used when thawed. Shelf life is approximately 12 months.
Technical data
Table 1 of 1
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Retention (Super Seal 2000 , At 200 ft² per gallon) | 0.21 | kg/m² | Test ASTM C309 |
| Moisture Retention (Test requirement, not to exceed) | 0.55 | kg/m² | Test ASTM C309 |
| Moisture Retention (Super Seal 2000 , At 300 ft² per gallon) | 0.32 | kg/m² | Test ASTM C309 |
| Moisture Retention (Test requirement, not to exceed, 300 ft² per gallon) | min. 0.4 | kg/m² | Test ASTM C309 |
| Gasoline Resistance (15-minute exposure, ponding) | Slight dulling | — | — |
| Tg | 50.0 | °C | — |
| Tukon Hardness (30 minutes at 180°F) | 9.3 | — | — |
| Tukon Hardness (30 minutes at 300°F) | 13.7 | — | — |
| Pencil Hardness (30 minutes at 180°F) | F | — | — |
| Pencil Hardness (30 minutes at 300°F) | H | — | — |
| Abrasion resistance (Lost, CS-17 wheel, 1000 g load, 1000 cycles) | 160.0 | mg | — |
| Flexibility (1/8 inch mandrel) | 6.0 | — | — |