Kopla KBG1010F
- Chemical Family
- Polyesters
Kopla KBG1010F is a Polybutylene Terephthalate (PBT) polymer which is reinforced with glass fiber.
Product families
Applications
Applications
- Electrical & Electronics — Other Electrical & Electronics Applications; Industrial — Other Industrial Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
Electrical & Electronics — Parts & Components
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 4500.0 - 4500.0 MPa
- Markets
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Characteristic
- Unfilled UL 94 V-0 Rating
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Plugs
- Relay Bases
- Sockets
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 80 | MPa | D638 |
| Flexural Modulus | 4500 | MPa | D790 |
| Flexural Strength | 135 | MPa | D790 |
| IZOD Impact Strength | 5 | KJ/m2 | D256 |
| Rockwell Hardness | 120 | Scale R | D785 |
| Tensile Elongation | 4 | x10-5 1/K | D696 |
| Tensile Modulus | 5100 | MPa | D790 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Thermal Expansion | 4 | x10-5 1/K | D696 |
| Flammability | V-0 | — | UL94 |
| Heat Deflection Temperature | 210 | °C | D648 |
| Melting Point | 225 | °C | DSC |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 1x10^17 | Ω.cm | D257 |
| Dielectric Constant | 3.4 | — | D150 |
| Dielectric Disspation | 0.01 | — | D150 |
| Dieletric Strength | 23 | — | D149 |
Table 4 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.5 | — | D792 |
| Water Absorption | 0.1 | % | D570 |
| Mold Shrinkage (3T) | 0.8-1.8 | % | D955 |