Kopla KNP1100
- Chemical Family
- Polyamides
Kopla KNP1100 is a Polyamide 6 (PA 6) polymer. It is processed by using applications.
Product families
Applications
Applications
- Industrial — Other Industrial Applications
Automotive & Transportation — Automotive
- Interior
- Other Automotive Applications
- Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Tooling & Moldmaking
Electrical & Electronics — Devices & Assemblies
- Automotive Electronics
- Other Devices & Assemblies
Industrial — Leather & Textiles
- Textile Manufacturing
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 2900.0 - 2900.0 MPa
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Characteristic
- Special lubricated, Easy releasing
- Material Features
- General Purpose
- Lubricated
- Plastics and Elastomers End Uses
- Buttons
- Connectors
- Gears
- Molds/Dies/Tools
- Power/Other Tools
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 29400 | MPa | D790 |
| Flexural Strength | 115 | MPa | D790 |
| IZOD Impact Strength | 4.5 | KJ/m2 | D256 |
| Rockwell Hardness | 120 | Scale R | D785 |
| Tensile Elongation | 100 | x10-5 1/K | D696 |
| Tensile Modulus | 2950 | MPa | D790 |
| Tensile Strength | 85 | MPa | D638 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability | V-2 | — | UL94 |
| Heat Deflection Temperature | 180 | °C | D648 |
| Melting Point | 222 | °C | DSC |
| Thermal Expansion | 7 | x10-5 1/K | D696 |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Constant | 3.4 | — | D150 |
| Dielectric Disspation | 0.02 | — | D150 |
| Dieletric Strength | 18 | — | D149 |
| Volume Resistivity | 1x10^15 | Ω.cm | D257 |
Table 4 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 1.7 | % | D570 |
| Density | 1.14 | — | D792 |
| Mold Shrinkage (3T) | 1.1-1.5 | % | D955 |
| Poisson's Ratio | 0.37 | % | D638 |