Kopla KDG1133CR
- Chemical Family
- Polyamides
Kopla KDG1133CR is a Polyamide 66 (PA 66) polymer which is reinforced with glass fiber.
Product families
Applications
Automotive & Transportation — Automotive
- Cooling & Climate
- Powertrain & UTH
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 8500.0 - 8500.0 MPa
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Characteristic
Rigidity, Glycol resistance, Hydrolysis resistance
- Material Features
- Good Glycol Resistance
- Good Rigidity
- High Hydrolysis Resistance
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 185 | MPa | D638 |
| Charpy Impact Strength | 95 | KJ/m2 | D256 |
| Flexural Modulus | 8500 | MPa | D790 |
| Flexural Strength | 250 | MPa | D790 |
| Rockwell Hardness | 120 | Scale R | D785 |
| Tensile Elongation | 3 | x10-5 1/K | D696 |
| Tensile Modulus | 10500 | MPa | D790 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Thermal Expansion | 2.5 | x10-5 1/K | D696 |
| Flammability | HB | — | UL94 |
| Heat Deflection Temperature | 250 | °C | D648 |
| Melting Point | 260 | °C | DSC |
Table 3 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 1x10^15 | Ω.cm | D257 |
| Dielectric Constant | 3.7 | — | D150 |
| Dielectric Disspation | 0.01 | — | D150 |
| Dieletric Strength | 32 | — | D149 |
Table 4 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption | 0.2 | % | D570 |
| Density | 1.37 | — | D792 |
| Mold Shrinkage (3T) | 0.3-+0.7 | % | D955 |