BioPBS™ FX85AC
- Chemical Family
- Polyesters
BioPBS™ FX85AC is a bio-based polybutylene succinate adipate (PBSA) produced through the polymerization of bio-based succinic acid, 1,4-butanediol, and adipic acid. Similar to LDPE, BioPBS™ is a soft and flexible semi-crystalline polyester with excellent properties that make it well-suited for cast extrusion and extrusion coating applications, including the production of compostable paper cups. FX85AC has been specifically developed for use in home compostable coated paper, catering to frozen and cold beverage applications.
Properties
- Physical Form
- Pellets
- Solid
Product families
- Biodegradable Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- BioPBS™
- Density
- 1,260.0 kg/m³
- Polymer Name
- Polybutylene Succinate Adipate (PBSA)
- Labeling Claims
Bio-based, Biodegradable, Food Contact Acceptable; Bio-based; Biodegradable; Food Contact Acceptable
- Processing Methods
- Extrusion, Extrusion Coating
- Notes
* Based on coating thickness 25 μm and paper weight 250 gsm under pressure 0.5 MPa for 1 second ** FX85AC is under testing for home compostable certificate.
- Technology
- Plastics
- Product Features
Similar processability as LDPE; Processable in LDPE extrusion coating machine; Excellent adhesion to paper; Superior heat sealability; Excellent printability without pre treatment; Low coating thickness; Bio content 40.45%; All components certified composability by BPI and TUV; Food contact approved by FDA (FCN No. 1818) and JHOSPA, and comply to EU10/2011
- Storage Condition
BioPBS™ pellet is dried and packed in aluminum-lined packaging before delivering to customers. Pre-dry of the unopened BioPBS™ is not necessary. It is recommended to keep packages sealed until ready to process and using up the whole 25-kg bag. Unused material should be tightly sealed, kept away from open air, and pre-dried (Temperature 80°C for over 5 hours) to moisture content of less than 1,000 ppm (preferable less than 700 ppm) prior to using next time. Do not store outdoors. Keep dry at ambient temperature. Avoid humid environment, heat and direct sunlight. Use material within 6 months after delivery date, in order to prevent possible material quality deterioration.
- Material Features
- Compostable
- Flexible
- Food Contact Acceptable
- Good Adhesion
- Good Printability
- Good Processability
- Heat Sealable
- Soft
- Certifications and Compliance
- EU Packaging Directive (94/62/EC)
- FDA Compliant
- Halal
- OK compost HOME
- OK compost INDUSTRIAL (EN 13432)
- TÜV Approved
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Extrusion Coating
Technical data
Table 1 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.26 | g/cm3 | ISO 1183 |
| Melt Flow Rate (190°C, 2.16 kg) | 15.0 | g/10 min | ISO 1133 |
| Melting Point | min. 84 | °C | ISO 3146 |
| Moisture Content | max. 1,000 | ppm | Karl Fischer |
| Seal Initiation Temperature* | 130.0 | °C | — |
| Service Temperature | max. 60 | °C | — |
| Home Compostable** | 1 - side and 2 - side coating | — | — |
Table 2 of 2
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 235 - 245 | °C |
| Feed Throat | 140.0 | °C |
| Barrel Temperature | 160 - 235 | °C |
| Adapter Temperature | 235 - 245 | °C |
| Die Temperature | 235 - 245 | °C |
| Chill Roll Temperature | max. 20 | °C |
| Air Gap | 10.0 | cm |
| Minimum Coating Weight | 20.0 | gsm |
| Corona Treatment | min. 8 | kW |