BioPBS™ FZ91PM/PB
BioPBS™ FZ91PM/PB is bio-based polybutylene succinate (PBS) produced from polymerization of bio-based succinic acid and 1,4-butanediol. Alike LDPE, BioPBSTM is soft and flexible semi-crystalline polyester with excellent properties suitable for blown and cast film extrusion.
Product families
Applications
- Food & Beverage Packaging
- Food & Beverage Packaging
Product Families
- Biodegradable Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- BioPBS™
- Density
- 1,260.0 kg/m³
- Polymer Name
- Polybutylene Succinate (PBS)
- Labeling Claims
Bio-based, Biodegradable, Food Contact Acceptable, From Renewable Resources; Bio-based; Biodegradable; Food Contact Acceptable; From Renewable Resources
- Processing Methods
- Blown Film Extrusion, Cast Film Extrusion
- Markets
- Food & Nutrition
- Printing & Packaging
- Technology
- Plastics
- Key Attributes
BioPBS™ containing renewable carbon.; BioPBS™ fully biodegradable even at ambient temperature and compostable (EN13432).; BioPBS™ compatible with end-of life both recycling (repulping operation) and composting even in backyard.; BioPBS™ is contribution to circular economy.; BioPBS™ safe for you and planet. It is food contact, approved by FDA, EU and JHOSPA.; BioPBS™ has processability similar to Polyethylene (PE).
- Product Features
Good processability and stable bubble in existing LDPE machine; Mulch films; No collection of the films after harvest for disposal or recycle. Bury into soil and gradually broken down into CO2, water and biomass; Suitable to other blown film applications, ie., bag liners, agricultural film, etc.; FZ91PM is food contact grade, approved by FDA (FCN No. 1817) and JHOSPA, comply to EU10/2011; OK COMPOST certified by TUV Austria in European Union, BPI in North America and ABA in Australia; Renewable content certified by DIN CERTCO, JBPA and USDA
- Quality Standards
- JCII
- Storage Condition
BioPBSTM pellet is dried and packed in aluminum-lined packaging before delivering to customers. Do not store outdoors. Keep dry at ambient temperature. Avoid humid environment, heat and direct sunlight. Use material within 6 months after delivery date, in order to prevent possible material quality deterioration. Pre-dry of the unopened BioPBSTM is not necessary. It is recommended to keep packages sealed until ready to process and using up the whole 25-kg bag. Unused material should be tightly sealed, kept away from open air, and pre-dried (Temperature 80°C for over 5 hours) to moisture content of less than 1,000 ppm (preferable less than 700 ppm) prior to using next time.
- Material Features
- Biodegradable
- Compostable
- Cost Effective
- Decomposable
- Durable
- Excellent Bubble Stability
- Excellent Initial Seal Strength
- Flexible
- Certifications and Compliance
- FDA Compliant
- Halal
- JHOSPA Registered
- OK compost HOME
- Regulation (EU) No. 10/2011 (PIM)
- TÜV Approved
- USDA Certified
- Plastics and Elastomers End Uses
- Agricultural Film
- Blown Films
- Boxes
- Cast Films
- Coffee Capsules
- Cups
- Cutlery
- Film
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Cast Film Extrusion
Technical data
Table 1 of 2
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Tensile Modulus (MD) | 575 | MPa | ISO 527-3 |
| Melt Flow Rate (at 190°C, 2.16 kg) | 5 | g/10 min | ISO 1133 |
| Tensile Modulus (TD) | 590 | MPa | ISO 527-3 |
| Melting Point | 115 | °C | ISO 3146 |
| Yield Stress (MD) | 39 | MPa | ISO 527-3 |
| Yield Stress (TD) | 38 | MPa | ISO 527-3 |
| Stress at Break (MD) | 42 | MPa | ISO 527-3 |
| Stress at Break (TD) | 30 | MPa | ISO 527-3 |
| Flexural Modulus | 650 | MPa | ISO 178 |
| Strain at Break (MD) | 350 | % | ISO 527-3 |
| Flexural Strength | 40 | MPa | ISO 178 |
Table 2 of 2
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Temperature | 140 - 160 | °C |
| Die Lip Gap | 0.8 - 1.0 | mm |
| Blow Up Ratio | 2 - 4 | — |