Duratron® T5530 PAI
- Chemical Family
- Polyamides
Duratron® T5530 PAI is a high-performance, glass-reinforced polyamide-imide material that offers exceptional rigidity, retention of stiffness, low thermal expansion, and outstanding load-carrying capabilities. This 30% glass-reinforced grade is ideal for structural applications in the semiconductor, electronics, and aerospace industries, where high strength, stiffness, and dimensional stability are required.Features:High rigidity and retention of stiffnessLow thermal expansionOutstanding load-carrying capabilities30% glass reinforced for added strength and stiffnessBenefits:Suitable for structural applications in harsh environmentsOffers exceptional dimensional stability up to 260°CIdeal for precision parts in the electronic and semiconductor industriesApplications:Aerospace and defenseSemiconductor and electronicsIndustrial machinery and equipmentMedical devicesPrecision parts in high-temperature environmentsNote: The suitability of Duratron T5530 PAI for sliding parts should be carefully evaluated as the glass fibers may cause abrasion to the mating surface.
Properties
- Physical Form
- Plates, Rods, Tube
- Plates
- Rods
- Tube
Other characteristics
- Brand
- Duratron® PBI, PEI, PAI
- Density
- 1,600.0 kg/m³
- Features
Creep Resistant, Dimensional Stability, Good Electrical Properties, Good Stiffness, High Loading Absorption Capability, High Rigidity, High Tolerance, Low Thermal Expansion, Odorless, Temperature Resistance
- Polymer Name
- Polyamide-imide (PAI)
- Tensile Modulus
- 6,892.0 MPa
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- Odor-free
- Fillers Included
- Glass Fiber
- Product Families
- Plastics — Parts, Shapes & Films
Technical data
Table 1 of 4
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 23000 | psi | ASTM D638 (8) |
| Tensile Strain (Elongation) at Break | 4 | % | ASTM D638 (8) |
| Tensile Modulus of Elasticity | 1000 | ksi | ASTM D638 (8) |
| Compressive Strength | 40000 | psi | ASTM D695 (11) |
| Izod Impact (Notched) | 1 | ft.lb./in | ASTM D256 |
| Flexural Strength | 30000 | psi | ASTM D790 (13) |
| Flexural Modulus of Elasticity | 980 | ksi | ASTM D790 |
Table 2 of 4
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glass Transition Temperature (DMA, Tan Delta) | 527 | °F | DMA |
| Thermal Conductivity (73°F) | 2.5 | BTU in./(hr. ft² ˚F) | — |
| Coefficient of Linear Thermal Expansion (-40 to 300°F) | 9 | µin./in./°F | ASTM E-831 (TMA) |
| Heat Deflection Temperature (Method A: 1.8 MPa (264 PSI)) | 530 | °F | ASTM D648 |
| Continuous Allowable Service Temperature in Air (20.000 hrs) (3) | 500 | °F | — |
| Flammability (3 mm) (5) | V-0 | — | UL 94 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Electric Strength | 700 | Volts/mil | ASTM D149 |
| Surface Resistivity | 10000000000000 | Ohm/sq. | ANSI/ESD STM 11.11 |
Table 4 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.6 | — | ASTM D792 |
| Water Absorption (After 24h Immersion in Water of 73°F) | 0.3 | % | ASTM D570 (17) |
| Water Absorption (At Saturation in Water of 73°F) | 1.5 | % | ASTM D570 (17) |