Forzeas™ DF9003
Forzeas™ DF9003 is certified as OK compost HOME, with a bio-based carbon content of 50% or more (estimated according to ASTM D6866). Designed for food contact applications, it has good processability in existing general machines and good rigidity comparable to PP. Examples of its application include straws for drinking.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
- Food & Beverage Packaging
Product Families
- Biodegradable Polymers
Other characteristics
- Brand
- Forzeas
- Polymer Name
- Polyester (unspecified)
- Labeling Claims
Bio-based, Biodegradable, Environmentally Friendly, Food Contact Acceptable, From Renewable Resources, Recyclable; Bio-based; Biodegradable; Environmentally Friendly; Food Contact Acceptable; From Renewable Resources; Recyclable
- Processing Methods
Extrusion, Extrusion Blow Molding (EBM), Profile Extrusion
- Markets
- Printing & Packaging
- Technology
- Plastics
- Packaging Type
- Bags
- Product Features
- Good processability in existing general machine.
- Good rigidity comparable to PP
- Storage Condition
FORZEAS™ pellets are dried and packed in aluminum-lined packaging before delivering to customers. Do not store outdoors. Keep dry at ambient temperature. Avoid humid environment, heat and direct sunlight. Use material as soon as possible after the delivery, in order to prevent possible material quality deterioration. Pre-dry of the unopened FORZEASTM is not necessary. It is recommended to keep packages sealed until ready to process and using up the whole 25-kg bag. Unused material should be tightly sealed, kept away from open air, and pre-dried (at 60 °C for over 5 hours).
- Color
- White
- Material Features
- Biodegradable
- Compostable
- Food Contact Acceptable
- Good Processability
- Good Rigidity
- Good Stiffness
- High Elasticity
- Recyclable
- Process Information
*The conditions are one example for straw molding. Please consult with us before your trial and production.
- Certifications and Compliance
- OK compost HOME
- Plastics and Elastomers End Uses
- Drinking Straws
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Extrusion Blow Molding (EBM)
- Profile Extrusion
Technical data
Table 1 of 1
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 160°C, 21.2 N) | 5.0 | g/10 min | ISO 1133 |
| Melt Flow Rate (at 160°C, 21.2 N) | 2.0 | g/10 min | ISO 1133 |
| Density | 1.45 | g/cm3 | ISO 1183 |
| Flexural Modulus | 1500.0 | MPa | ISO 178 |
| Heat Deflection Temperature (at 0.45 MPa) | 70.0 | °C | ISO 75 |