Forzeas™ DA9013
- Chemical Family
- Polyesters
Forceas™ DA9013 is certified as OK compost HOME. It is a soft polyester with excellent properties, suitable for both blown and cast film. Forceas™ DA9013 is also suitable for food-contact applications. Features include good processability in existing LDPE machines and suitability as a sealant layer for flexible packaging as well as for blown film applications such as bags.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
- Food & Beverage Packaging
Product Families
- Biodegradable Polymers
Other characteristics
- Brand
- Forzeas
- Polymer Name
- Polyester (unspecified)
- Labeling Claims
Bio-based, Biodegradable, Environmentally Friendly, Food Contact Acceptable, From Renewable Resources, Recyclable; Bio-based; Biodegradable; Environmentally Friendly; Food Contact Acceptable; From Renewable Resources; Recyclable
- Processing Methods
Blown Film Extrusion, Cast Film Extrusion, Extrusion, Film Extrusion, Profile Extrusion
- Markets
- Printing & Packaging
- Technology
- Plastics
- Packaging Type
- Bags
- Product Features
Good processability in existing LDPE machines; Suitable as sealant layer for flexible packaging; Suitable to blown film applications, i.e. bags etc.
- Storage Condition
FORZEAS™ pellets are dried and packed in aluminum-lined packaging before delivering to customers. Do not store outdoors. Keep dry at ambient temperature. Avoid humid environment, heat and direct sunlight. Use material as soon as possible after the delivery, in order to prevent possible material quality deterioration. Pre-dry of the unopened FORZEAS™ is not necessary. It is recommended to keep packages sealed until ready to process and using up the whole 25-kg bag. Unused material should be tightly sealed, kept away from open air, and pre-dried (at 60 °C for over 5 hours).
- Color
- White
- Material Features
- Biodegradable
- Compostable
- Food Contact Acceptable
- Recyclable
- Process Information
Roll temp.: 25-35 °C; *The conditions are one example for film fabrication. Please consult with us before your trial and production.
- Plastics and Elastomers End Uses
- Compost Bag
- Shopping Bags
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blown Film Extrusion
- Cast Film Extrusion
- Extrusion
- Film Extrusion
- Profile Extrusion
Technical data
Table 1 of 1
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 160°C, 21.2 N) | 5.0 | g/10 min | ISO 1133 |
| Density | 1.24 | g/cm3 | ISO 1183 |
| Young Modulus (MD) | 410.0 | MPa | ISO 527-3 |
| Young Modulus (TD) | 390.0 | MPa | ISO 527-3 |
| Yield Stress (MD) | 16.0 | MPa | ISO 527-3 |
| Yield Stress (TD) | 16.0 | MPa | ISO 527-3 |
| Tensile Strength (MD) | 44.0 | MPa | ISO 527-3 |
| Elongation at Beak (MD) | 770.0 | % | ISO 527-3 |
| Elmendorf Tear Strength (MD) | 3.0 | N/mm | ISO 6383-2 |
| Puncture Impact Strength | 20000.0 | J/m | MCC method |
| Bio-based Content (Calculated) | 40.0 | % | ASTM D6866 |
| Thickness | 30.0 | μm | — |