Zortrax BlueCast X10 LCD/DLP
Advanced castable 3D printing resin designed to guarantee smooth surfaces and precise details in relatively big models. BlueCast X10 makes it possible to print jewelry pieces requiring large amounts of metal. It exhibits properties nearly identical to wax and thus can be processed with the same toolset. Full burnout is possible at a relatively low temperature of 740° C. The resin requires post-curing only when post processing techniques like polishing are to be applied to the 3D printed pattern. Otherwise, post-curing is not necessary. Storing a pattern for 7 days causes a negligible 0.7% shrinkage which is particularly useful when patterns need to be made in advance. The resin can lose color when exposed to UV light. It is completely normal and does not affect its specified properties.
Product families
Applications
- Consumer Goods — Other Consumer Goods Applications
- Digital Printing
Product Families
- Photoactive Resins
Other characteristics
- End Uses
- Consumer Applications, Jewelry
- Polymer Name
- Thermoplastic (unspecified)
- Processing Methods
- 3D Printing, Digital Light Processing
- Color
- Blue
- Markets
- Consumer Goods
- Printing & Packaging
- Features
Large investment pattern; Clean burnout; Smooth surfaces; Smooth surfaces and dimensional accuracy make it possible to print large investment patterns.; Negligible shrinkage; Investment patterns can be 3D printed in advance as the resin shrinks only 0.7% in 7 days.
- Technology
- Plastics
- Packaging Type
- Bottles
- Available Colours
- Transparent Blue
- Material Features
- Excellent Dimensional Accuracy
- Good Smoothness
- Low Shrinkage
- Plastics and Elastomers End Uses
- Consumer Applications
- Jewelry
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- 3D Printing
- Digital Light Processing
Technical data
Table 1 of 1
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Burnout Temperature | min. 740 | °C |
| Shrinkage (7 Days) | 0.7 | % |
| Ash Content (Residue After Burnout) | 0 | % |