Viva Nylons LimitedViva Nylons Limited PA6C Moly
Viva Nylons Limited PA6C Moly contains improved crystallization and a degree of self-lubrication through the addition of molybdenum disulphide. Hardness increases and simultaneously the general mechanical and anti-friction properties are improved.
Color:
- Black
Density:
- 1150.0 - 1150.0 kg/m³
Features:
- Dimensional Stability, Friction Resistant, Good Machinability, Good Mechanical Properties, High Degree of Crystallinity, High Hardness, High Temperature Strength, Lubricated, Self Lubricating
Polymer Name:
- Polyamide 6 (PA 6)
Physical Form:
- Custom, Plates, Rods, Tube
- Custom
- Plates
- Rods
- Tube
Tensile Modulus:
- 4100.0 - 4100.0 MPa
Markets:
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
Flame Rating:
- IEC 60695-11-10 HB
Technology:
- Plastics
Chemical Family:
- Polyamides
Product Families:
- Plastics — Parts, Shapes & Films
Additives Included:
- Lubricant (Molybdenum Disulfide)
Material Features:
- Dimensional Stability
- Friction Resistant
- Good Machinability
- Good Mechanical Properties
- High Degree of Crystallinity
- High Hardness
- High Temperature Strength
- Lubricated
- Self Lubricating
Benefits and Features:
- Improved Cystallisation - Molybdenum Disulphide is added resulting in improved crystallization. This process increases the superficial hardness of the material, improving its anti-friction & dimensional stability properties.
- Suitable for High Operating Temperatures - The crystal structure of PA6 Moly breaks down immediately before the melting temperature is reached, the thermal properties of the Moly are improved over standard PA6 grade. To learn more view the product technical information.
- Excellent Machining Properties - The increased superficial hardness provides Moly with excellent machinability and general mechanical properties.
Plastics and Elastomers End Uses:
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Housings
- Sporting Goods
Applications
Applications
- Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
- Other Automotive Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
| Characteristic name | Value | Unit of measurement | Test method |
| Tensile Strength at Yield (Sample Type 1B, 50mm/min) | 85.0 | MPa | ISO 527-1/2;1993 |
| E-modulus (Sample Type 1B, 50mm/min) | 4100.0 | MPa | ISO 527-1/2:1993 |
| Elongation at Break (Sample Type 1B, 50mm/min) | max. 20 | % | ISO 527-1/2:1993 |
| Compressive Strength (Sample Type B, 5mm/min) | 105.0 | MPa | ISO 604:2002 |
| Compressive Modulus (Sample Type A, 1mm/min) | 3000.0 | MPa | ISO 604:2002 |
| Flexural Strength (1.5mm/min) | 115.0 | MPa | ISO 178:2001 |
| Flexural Modulus (1.5mm/min) | 3700.0 | MPa | ISO 178:2001 |
| Izod Impact Strength (Sample Type A, notched) | 4.5 | kJ/mm² | ISO 180:2000 |
| Dynamic Coefficient of Friction (31.4m/min, 1.75MPa) | 0.25 | - | - |
| K-Factor (Wear Factor, 31.4m/min, 1.75MPa) | 2.2x10⁻⁵ | mm³/Nm | - |
| Hardness | 85.0 | Shore D | ISO 868:2003 |
| Characteristic name | Value | Unit of measurement | Test method |
| Density (Test Method A) | 1.15 | g/cm³ | ISO 1183:1987 |
| Water Absorption (24 hrs, Immersion at 23°C) | 0.2 | % | ISO 62:1999 (modified) |
| Water Absorption (24 hrs Saturation, Immersion at 23°C) | 6.0 | % | ISO 62:1999 |
| Characteristic name | Value | Unit of measurement | Test method |
| Melting Temperature (Tg) | 220.0 | °C | - |
| Glass Transition Temperature | 68.0 | °C | ISO 11359:1999 |
| Heat Deflection Temperature (HDT/A, 1.80MPa) | 80.0 | °C | ISO 75 |
| Maximum/Minimum Continuous Service Temperatures | 105/-40 | °C | - |
| Maximum/Minimum Intermittent Service Temperatures | 170/-100 | °C | - |
| Coefficient of Linear Thermal Expansion (23 - 55°C) | 8x10⁻⁵ | °C⁻¹ | ISO 11359-2:1999 |
| Thermal Conductivity (Mean T = 20°C) | 0.26 | W/m°C | ISO 8301:1991 |
| Characteristic name | Value | Unit of measurement | Test method |
| Dielectric Constant (1MHz) | 3.7 | - | IEC 60250:1969-01 |
| Dielectric Constant (Low Frequency, 100 Hz) | 4.0 | - | IEC 60250:1969-01 |
| Dielectric Strength | 25.0 | kV/m | IEC 60243:-1:1998-01 |
| Volume Resistivity | 1x10¹³ | ohm.m | IEC 60093:1980-01 |
| Surface Resistivity | 1x10¹² | ohm.m | IEC 60093:1980-01 |
| Comparative Tracking Index | 600.0 | CTI | IEC 60112:2003-01 |
| Characteristic name | Value | Unit of measurement | Test method |
| Flammability | HB | - | IEC 60695-11-10:2003-08 |