NYPOL® A3 G30 HS RH UV PRTA011 NR393K
- Chemical Family
- Polyamides
NYPOL® A3 G30 HS RH UV PRTA011 NR393K is a 6.6 black polyamide with 30% thermostable fiberglass with UV protection
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- NYPOL
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 12200.0 - 12200.0 MPa
- Processing Methods
- Extrusion, Injection Molding
- Color
- Black
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Appearance
- Black
- Properties
- Fiberglass composites with up to 50% filler.
- Flame propagation resistance: GWT 960 °C.
- Development of specific colors with Nylon base.
- Additives for UV protection applications.
- Applications
Automotive & Transportation — Other Automotive & Transportation Applications; Building & Construction — Other Building & Construction Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications
- Key Features
- Hydrolysis Resistant
- Glycol Resistant
- Filled, Glass Fiber
- Heat stabilized
- Mechanical Properties, Good
- Thermal Stability, Good
- Technology
- Plastics
- Material Features
- Good Electrical Properties
- Good Mechanical Properties
- Good Processability
- Good Surface Appearance
- Good Thermal Stability
- Good UV Protection
- High Productivity
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 200 | MPa | ASTM D638 |
| Flexural Modulus | 12200 | MPa | ASTM D790 |
| Flexural Modulus | 210 | MPa | ASTM D790 |
| Flexural Strength | 210 | MPa | ASTM D790 |
| Hardness (Ball Indentation) | 230 | MPa | ASTM D 785 |
| Impact Strength (Notched Charpy) | 12 | kJ/m² | ASTM D 256 |
| Impact Strength (Notched Izod) | 10 | kJ/m² | ASTM D 256 |
| Impact Strength (Notched Izod) | 11 | kJ/m² | ASTM D 256 |
| Tensile Elongation at Break | 3.2 | % | ASTM D638 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Linear Mold Shrinkage | 0.3 | % | ASTM D 955 |
| Humidity Absorption | 1.5 | % | — |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Point | 250 - 265 | °C | ASTM D 2117 |
| Heat Deflection Temperature (1.80Mpa, Unannealed) | 250 | °C | ASTM D648 |
| Flame Rating | HB | — | UL94 |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ash Content | 28 - 32 | % | ASTM D 2584 |
| Apparent Density | 1.36 - 1.38 | g/cm³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.3 | % | ASTM D 955 |
| Humidity Absorption | 1.5 | % | — |
| Flame Rating | HB | — | UL94 |
| Relative viscosity (Formic Acid) | 46 - 52 | — | — |
Table 5 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength | 36 | kV.mm-1 | ASTM D149 |
| Surface Resistivity | 10¹³ | ohm | IEC 60093 |
| Volume Resistivity | 10¹¹ | ohm·cm | IEC 60093 |