NYPOL® A3 G50 NTLA010 NR308
- Chemical Family
- Polyamides
NYPOL® A3 G50 NTLA010 NR308 is a Natural 6.6 polyamide with 50% glass fibers
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- NYPOL
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Extrusion, Injection Molding
- Color
- Natural
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Properties
- Fiberglass composites with up to 50% filler.
- Flame propagation resistance: GWT 960°C.
- Development of specific colors with Nylon base.
- Additives for UV protection applications.
- Applications
Automotive & Transportation — Other Automotive & Transportation Applications; Building & Construction — Other Building & Construction Applications; Consumer Goods — Other Consumer Goods Applications; Electrical & Electronics — Other Electrical & Electronics Applications
- Flame Rating
- UL 94 HB
- Key Features
Good chemical, physical and electrical properties.
- Technology
- Plastics
- Material Features
- Good Electrical Properties
- Good Mechanical Properties
- Good Processability
- Good Surface Appearance
- High Productivity
- Certifications and Compliance
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Color | Natural | — | — |
| Drying (90°C) | 4 | Hours | — |
| Stress at Break (Cond.) | 180 | MPa | ISO 527 |
| Tensile Modulus (Cond.) | 13000 | MPa | ISO 527 |
| Tensile Modulus (Dry) | 17000 | MPa | ISO 527 |
Table 2 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Strength (Cond.) | 250 | MPa | ISO 178 |
| Flexural Strength (Dry) | 345 | MPa | ISO 178 |
| Izod Notched Impact Strength (23°C, Cond.) | 18 | kJ/m² | ISO 180/A |
| Izod Notched Impact Strength (23°C, Dry) | 14 | kJ/m² | ISO 180/A |
| Stress at Break (Dry) | 245 | MPa | ISO 527 |
Table 3 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Flame Rating (3.2mm) | HB | — | UL94 |
| Humidity Absorption (Cond.) | 1.2 | % | ISO 62 |
| Melting Point | 263 | °C | ISO 75-1-2 |
| Molding Process Temperature | 270 - 290 | °C | — |
| Mold Shrinkage (Dry, Flow, 3.18mm) | 0.8 | — | ISO 294-4 |
| Mold Shrinkage (Dry, Parallel, 3.18mm) | 0.3 | — | ISO 294-4 |
| Water absorption (Cond.) | 4.2 | % | ISO 62 |
Table 4 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (1.80MPa) | 244 | °C | — |
| Mold Temperature | 60 - 90 | °C | — |
| Strain at Break (Cond.) | 3.2 | % | ISO 527 |
| Strain at Break (Dry) | 2.3 | % | ISO 527 |