To catalogue
UNITHANE HS-1007
- CASE Ingredients Features
- Excellent AdhesionGood Hydrolysis ResistanceImproved Flexibility
- Chemical Family
- Polyurethanes (PU)
UNITHANE HS-1007 is a high solids, solvent free, APEO free waterbased polyurethane dispersion with superior flexibility and recovery properties. UNITHANE HS-1007 is designed for both interior and exterior industrial coating applications requiring flexibility, adhesion and hydrolysis resistance.
Properties
- Physical Form
- Dispersion
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications
Paints & Coatings — Building & Construction
- Architectural Coatings
- Floor Coatings
- Wood Coatings & Finishes
Building & Construction — Building Envelope & Roofing
- Architectural Coatings
Building & Construction — Flooring & Surfaces
- Floor Coatings
Paints & Coatings — Industrial Coatings
- Industrial Coatings
Product Families
CASE Ingredients — Resins & Binders
- Polyurethanes (PU)
Other characteristics
- Brand
- UNITHANE
- End Uses
Solventless & High Solids Coating, Waterborne Adhesive, Waterborne Coating
- Features
Excellent Adhesion, Good Hydrolysis Resistance, Improved Flexibility; Solvent Free (SF); NMP-Free (NF); Low VOC (<100 g/L)
- Markets
- Adhesives & Sealants
- Building & Construction
- Paints & Coatings
- Appearance
- Opaque
- Shelf LIfe
- max. 12
- Coating Type
- Solventless & High Solids Coating
- Waterborne Coating
- Technology
- CASE Ingredients
- Labeling Claims
- APEO-Free
- Product Type
- Interior
- Exterior
- Flooring
- Wood
- Paint
- OPV
- Paper
- Textiles
- Adhesive & Sealant Type
- Waterborne Adhesive
- Chemical Resistance
- Chemical Resistance Testing (D-1308):
- WATER
- 5
- ACETIC ACID
- 5
- AMMONIA
- 5
- METHYL ETHYL KETONE
- 2
- 2-PROPANOL
- 3
- TOLUENE
- 4
- GASOLINE
- 5
- Various Substrate Cross-cut Adhesion
- Various Substrate Cross-cut Adhesion (D-3359)
- COLD ROLL STEEL - UNPOLISHED
- 5B
- ALUMINUM - UNTREATED
- 3B
- BRASS - UNTREATED
- 5B
- ABS - UNTREATED
- 5B
- POLYCARBONATE - UNTREATED
- 5B
- NYLON - UNTREATED
- 0B
- HDPE - UNTREATED
- 0B
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Total Solids | 54 - 56 | — | — |
| pH | 8.0 - 9.5 | — | — |
| Viscosity at 25°C | 500 - 1500 | cps | — |
| VOC | 10 | g/l | — |
| VOC (Total Weight) | 1 | % | — |
| Specific Gravity | 1.03 | — | — |
| Gloss at 60°C | 30 - 90 | — | — |
| Freezethaw Cycles | 3 | — | D2243 |
| Harmonize tariff number | 3909.50.6000 | — | — |
Table 2 of 2
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile | 2410 | psi | D-882 |
| Elongation | 2070 | % | D-882 |
| Cold crack | below -30 | °C | ISO 17233 |
| Softening point | 140 | °C | — |
| Pencil hardness | 2 | h | D-3363 |
| Sward hardness | 4.8 | — | D-2134 |
| Uv resistance (1000 hours at 340 nm) | No damage | — | D-4587 |
| Impact resistance | No damage at 160 psi direct, damage at 160 psi reverse | — | D-2794 |
| Tabor abrasion | n/a | — | D-4060 |
| Mandrel bend | pass 1/8, 1/4, 3/8, 1/2, 5/8, 3/4, 1 | — | D-522 |
| Hydrolysis resistance (200 hours, 70ºc, 95% rh) | Retained 100% of tensile properties | — | — |
| Hydrolysis resistance (200 hours, 70ºc, 95% rh) | Retained 100 | % | — |