To catalogue
UNITHANE IC-922 NF
- CASE Ingredients Features
- Improves AdhesionLow VOC
- Chemical Family
- Polyurethanes (PU)
UNITHANE IC-922 NF is a NMP free, low VOC waterbased polyurethane with exceptional adhesion promoting properties. UNITHANE IC-922 NF is designed for use in a formulated primer coat for variety of substrates.
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications
Paints & Coatings — Building & Construction
- Concrete Coatings & Stains
- Floor Coatings
Building & Construction — Flooring & Surfaces
- Floor Coatings
Printing & Packaging — Packaging Coatings
- Primers & Lacquers
Paints & Coatings — Packaging Coatings
- Primers & Lacquers
Product Families
CASE Ingredients — Resins & Binders
- Polyurethanes (PU)
Other characteristics
- Brand
- UNITHANE
- End Uses
- Primer, Waterborne Coating
- Features
- Improves Adhesion, Low VOC
- NMP-Free (NF), Low VOC (<100 g/L)
- Compatible Substrates & Surfaces
- Concrete
- Markets
- Adhesives & Sealants
- Building & Construction
- Paints & Coatings
- Printing & Packaging
- Appearance
- Semi-translucent, Clear after curing
- Shelf LIfe
- max. 12
- Coating Type
- Primer
- Waterborne Coating
- Technology
- CASE Ingredients
- Labeling Claims
- Low VOC
- NMP-free
- Product Type
- Interior, Exterior, Flooring, Concrete
- Chemical Resistance
- Chemical Resistance Testing (D-1308):
- WATER
- 5
- ACETIC ACID
- 3
- AMMONIA
- 2
- METHYL ETHYL KETONE
- 1
- 2-PROPANOL
- 2
- TOLUENE
- 4
- GASOLINE
- 5
- Compatible Substrates and Surfaces
- Concrete
- Various Substrate Cross-cut Adhesion
- Various Substrate Cross-cut Adhesion (D-3359)
- COLD ROLL STEEL - UNPOLISHED
- 5B
- ALUMINUM - UNTREATED
- 5B
- BRASS - UNTREATED
- 5B
- ABS - UNTREATED
- 5B
- POLYCARBONATE - UNTREATED
- 5B
- NYLON - UNTREATED
- 5B
- HDPE - UNTREATED
- 0B
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Total Solids | 31 - 33 | — | — |
| pH | 7.0 - 8.0 | — | — |
| Viscosity at 25°C | 500 - 1000 | cps | — |
| VOC | 45.17 | g/l | — |
| VOC (Total Weight) | 4.52 | % | — |
| Specific Gravity | 1.03 | — | — |
| Gloss at 60°C | 80 - 100 | — | — |
| Freezethaw Cycles | 0 | cycles | D2243 |
| Harmonize tariff number | 3909.50.6000 | — | — |
Table 2 of 2
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile | 3850 | psi | D-882 |
| Tensile at 100% Elongation | 600 | psi | — |
| Elongation | 1000 | % | D-882 |
| Cold crack | below -30 | °C | ISO 17233 |
| Softening point | 130 | °C | — |
| Pencil hardness | max. 6B | h | D-3363 |
| Sward hardness | 2 | — | D-2134 |
| Uv resistance (1000 hours at 340 nm) | No damage | — | D-4587 |
| Impact resistance (Direct or Reverse) at 160 psi | N0 Damage | — | D-2794 |
| Tabor abrasion (Loss) (CS-10, 1000 cycles) | 13 | mg | D-4060 |
| Mandrel bend at 1/8 | Pass 1/8, 1/4, 3/8, 1/2, 5/8, 3/4, 1 | — | D-522 |
| Dry Time | 35 | minutes | D-5895 |