Armlen PP E/P 15-2LS
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Armlen PP E/P 15-2LS is a impact modified, light-stabilized polypropylene. This material displays high resistance to impact, including impacts in low temperature environment; high elasticity, frost-resistance and resistance to alternating loads. Designed for bumper manufacture and number of car lining parts, available for further dye with enamels. Available in natural, black, natural, light-gray, gray and graphite.
Product families
Applications
Automotive & Transportation — Automotive
- Exterior & Body
- Interior
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- R&P POLYPLASTIC Armlen
- Polymer Name
- Polypropylene (unspecified)
- Melt Flow Index
- 6.0 - 6.0 g/10 min
- Color
- Black
- Grey
- Natural
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Material Features
- Frost Resistant
- High Elasticity
- Impact Modified
- Impact Resistance
- Light Stabilized
- Low Temperature Impact Resistance
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Point | 160 | °C | ISO 11357 |
| Deflection Temperature at 1.8 MPa load | 50 | °C | ISO 75 |
Table 2 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Volume Resistivity | 1.00+E13 | Ω⋅m | IEC 60093 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (250°C, 2.16 kg) | 6 | g/10 min | ISO 1133 |
| Melt Temperature | 190 | °C | — |
| Mold Temperature | 65 | °C | — |
| Moulding Shrinkage, parallel | 1.4-1.6 | % | ISO 294-4 |
| Moulding Shrinkage, normal | 1.4-1.6 | % | ISO 294-4 |
Table 4 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 900 | kg/m3 | ISO 1183 |
| Indentation Hardness by Means of a Durometer (Shore Hardness) | 59 | Shore D | ISO 868 |
| Yield Stress | 24 | 50mm/min | ISO 527 |
| Strain at Break | 360 | % | ISO 527-1 |
| Flexural Stress at maximum load | 23 | MPa | ISO 178 |
| Tensile Modulus | 900 | MPa | ISO 178 |
| Charpy Impact Strength at +23°C (un-notched) | No break | kJ/m2 | ISO 179-1 |
| Charpy Impact Strength at -50°C (un-notched) | 70 | kJ/m2 | ISO 179-1 |
| Charpy Impact Strength at +23°C (notched) | 11 | kJ/m2 | ISO 179-1 |