Tarnoform® 200 HI4
Grade with increased impact strength ISO 9988-1: POM-K, M-GNPR, 01-001
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- Tarnoform
- Polymer Name
- Polyacetal Copolymer (POM)
- Flexural Modulus
- 1400.0 - 1400.0 MPa
- Processing Methods
- Extrusion, Injection Molding
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- High Viscosity
- Impact Resistance
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Strain at Break | min. 50 | % | ISO 527 |
| Tensile Modulus | 1600 | MPa | ISO 527 |
| Yield stress | 42 | MPa | ISO 527 |
| Yield strain | 20 | % | ISO 527 |
| Flexural modulus, 23° | 1400 | MPa | ISO 178 |
| Charpy impact strength (+23°) | N | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 25 | kJ/m2 | ISO 179/1eA |
| Izod notched impact strength, +23° | 30 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 80 | MPa | ISO 2039-1 |
Table 2 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (190°C/2.16 kg) | 3 | g/10 min | ISO 1133 |
| Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 3 | g/10 min | ASTM D1238 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 2.5 | cm3/10 min | ISO 1133 |
| Moisture Absorption (23°C/50% RH) | 0.3 | % | ISO 62 |
| Density | 1330 | kg/m3 | ASTM D 792 |
Table 3 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 110 | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 70 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 70 | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 167 | °C | ISO 11357-1-3 |
| Vicat Softening Temperature (50 N) | 115 | °C | ISO 306 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 | mm | — |
| Vicat softening temperature | 115 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Humidity absorption | 0.3 | % | Sim. to ISO 62 |