Tarnamid® T- 27 CF10
- Chemical Family
- Polyamides
Tarnamid® T- 27 CF10 is a 10% carbon fiber reinforced polyamide 6 compound, heat stabilized, good conductive and electrostatic properties.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Industrial — Oil, Gas & Mining
- Mining
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 6700.0 - 6700.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Industrial
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Anti-Static
- Electrically Conductive
- Heat Stabilized
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Mining Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 130 / - | MPa | ISO 527 |
| Tensile Modulus | 8000 / - | MPa | ISO 527 |
| Strain at break | 4.5 / - | % | ISO 527 |
| Flexural modulus, 23° | 6700 / - | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 3 / - | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 42 / - | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 3.5 / - | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 200 / - | MPa | ISO 2039-1 |
Table 2 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 60 | cm3/10min | ISO 1133 |
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 60 / * | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 9 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 3/0 | % | ISO 294-4 |
| Molding shrinkage - parallel | 0.3 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - normal | 0.9 / * | % | ISO 294-4, 2577 |
| Density | 1160 / - | kg/m3 | ISO 1183 |
Table 3 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Delfection Temperature Under Load (1.8 MPa) | 190 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 190 / * | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50 N) | 200 | °C | ISO 306 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 1.6 / * | mm | — |
| Vicat softening temperature | 200 / * | °C | ISO 306 |
| Burning Behavior at 1.5 mm nominal thickness | HB / * | class | IEC 60695-11-10 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Table 4 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity | 1.00E+07 | ohm | ASTM D257 |
| Volume Resistivity | 10000000 | ohm.m | ASTM D257 |