Tarnamid® T- 27 GF35 P5
- Chemical Family
- Polyamides
Tarnamid® T-27 GF35P5 is tribological modified grade, which cause decrease coefficient of friction and wear. ISO 1874-1: PA 6, MHR, 14-080, GF30Z
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Tarnamid
- Polymer Name
- Polyamide 6 (PA 6)
- Flexural Modulus
- 10000.0 - 10000.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Low Friction
- Tribological Modified
- Wear Resistant
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Construction Applications
- Electrical/Electronic Applications
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 160 / - | MPa | ISO 527 |
| Tensile Modulus | 12000 / - | MPa | ISO 527 |
| Strain at break | 1.5 / - | % | ISO 527 |
| Flexural modulus, 23° | 10000 / - | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 7 / - | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 50 / - | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 8 / - | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 270 / - | MPa | ISO 2039-1 |
Table 2 of 4
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (275°C/5 kg) | 15 / * | cm3/10 min | ISO 1133 |
| Molding shrinkage - normal | 1.1 / * | % | ISO 294-4, 2577 |
| Molding shrinkage - parallel | 0.1 / * | % | ISO 294-4, 2577 |
| Density | 1470 / - | kg/m3 | ISO 1183 |
Table 3 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (1.80 Mpa) | 210 / * | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 / * | mm | — |
| Vicat softening temperature | 215 / * | °C | ISO 306 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Table 4 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 550 | V | IEC 6112 |