Tarnoform® 500 GF6
Grupa Azoty S.A Tarnoform® 500 GF6 is a 30% glass fibers reinforced injection-molding easy flowing grade with very high strength and stiffness and reduced shrinkage and coefficient of linear thermal expansion.
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Applications
- Consumer Goods — Housewares
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
Electrical & Electronics — Devices & Assemblies
- Other Devices & Assemblies
Product Families
Plastics — Engineering & Specialty Polymers
- Polyacetals
Other characteristics
- Brand
- Tarnoform
- Polymer Name
- Polyacetal Copolymer (POM)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 9000.0 - 9000.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- High Flow
- High Stiffness
- High Strength
- Low Shrinkage
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Automotive Applications
- Construction Applications
- Electrical/Electronic Applications
- Household Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength | 115 | MPa | ISO 527 |
| Tensile Modulus | 9500 | MPa | ISO 527-2/1A/1 |
| Strain at break | 1.7 | % | ISO 527 |
| Flexural modulus, 23° | 9000 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 5 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 25 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 5 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 220 | MPa | ISO 2039-1 |
Table 2 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Index - MFI (190°C/2.16 kg) | 6 | g/10 min | ASTM D 1238 |
| Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 4.5 | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 7/1 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 3 | % | ISO 294-4 |
| Molding shrinkage - parallel | 0.7 | % | ISO 294-4, 2577 |
| Molding shrinkage - normal | 1.3 | % | ISO 294-4, 2577 |
| Water Absorption (23/sat.) | 0.8 | % | ISO 62 |
| Moisture Absorption (23°C/50% RH) | 0.17 | % | ISO 62 |
| Density | 1630 | kg/m3 | ISO 1183 |
Table 3 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 40 | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 80 | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 160 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 160 | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 167 | °C | ISO 11357-1-3 |
| Vicat Softening Temperature (50 N) | 155 | °C | ISO 306 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 | mm | — |
| Vicat softening temperature | 155 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index - CTI | 600 | V | UL 746 |
| Surface Resistivity | 1.00E+13 | ohm | IEC 60093 |
| Volume Resistivity | 100000000000000.0 | ohm.m | ASTM D 257 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 0.8 | % | Sim. to ISO 62 |
| Humidity absorption | 0.17 | % | Sim. to ISO 62 |